Based on material design idea,we employ a co-precipitation strategy to obtain sinterable Ho_(2)Zr_(2)O_(7) flu-orite particles,successfully leading to novel transparent Ho_(2)Zr_(2)O_(7) ceramics with good optical/mag...Based on material design idea,we employ a co-precipitation strategy to obtain sinterable Ho_(2)Zr_(2)O_(7) flu-orite particles,successfully leading to novel transparent Ho_(2)Zr_(2)O_(7) ceramics with good optical/magneto-optical properties.The resulting precipitation precursor is identified to be hydrated basic carbonate upon calcination at the optimum temperature of 1250℃into near-spherical Ho_(2)Zr_(2)O_(7) nanopowder with an average size of~64 nm and unimodal narrow size distribution.The crystal intrinsic oxygen defect in fluorite ceramic generally exists in the form of F+center.The best bulk specimen achieved in this work exhibits a high refractive index of~2.1 and a high transparency of~74.4%at 1000 nm comparable with the corresponding defect-free single crystal(~76.4%in theory).In the Ho_(2)Zr_(2)O_(7) structure system,the elec-tronic polarizability of O_(2)-anion generally remains constant around 2.2?3 in the visible region and the corresponding optical basicity is approximately 0.9.The developed magneto-optical transparent Ho_(2)Zr_(2)O_(7) ceramic has Verdet constants of-180±3,-157±5,-87±2,-54±2,and-43±2 rad T^(-1) m^(-1) at 515,635,780,980,and 1064 nm,respectively,which are roughly 1.2-fold higher than the commercial TGG crystal.展开更多
基金supported by the Zhejiang Provincial Natural Science Foundation of China (Grant No.LY23F050007)the Department of Education of Zhejiang Province (No.Y202146207).
文摘Based on material design idea,we employ a co-precipitation strategy to obtain sinterable Ho_(2)Zr_(2)O_(7) flu-orite particles,successfully leading to novel transparent Ho_(2)Zr_(2)O_(7) ceramics with good optical/magneto-optical properties.The resulting precipitation precursor is identified to be hydrated basic carbonate upon calcination at the optimum temperature of 1250℃into near-spherical Ho_(2)Zr_(2)O_(7) nanopowder with an average size of~64 nm and unimodal narrow size distribution.The crystal intrinsic oxygen defect in fluorite ceramic generally exists in the form of F+center.The best bulk specimen achieved in this work exhibits a high refractive index of~2.1 and a high transparency of~74.4%at 1000 nm comparable with the corresponding defect-free single crystal(~76.4%in theory).In the Ho_(2)Zr_(2)O_(7) structure system,the elec-tronic polarizability of O_(2)-anion generally remains constant around 2.2?3 in the visible region and the corresponding optical basicity is approximately 0.9.The developed magneto-optical transparent Ho_(2)Zr_(2)O_(7) ceramic has Verdet constants of-180±3,-157±5,-87±2,-54±2,and-43±2 rad T^(-1) m^(-1) at 515,635,780,980,and 1064 nm,respectively,which are roughly 1.2-fold higher than the commercial TGG crystal.