A transparent and antistatic coating material consisting of polymer core-metal shell particle was prepared. As a polymer core, poly(butylacrylate-co-styrene)s ([P(BA-co-sty)s]) with various compositions of butylacryla...A transparent and antistatic coating material consisting of polymer core-metal shell particle was prepared. As a polymer core, poly(butylacrylate-co-styrene)s ([P(BA-co-sty)s]) with various compositions of butylacrylate and styrene were synthesized by emulsion polymerization. And the effect of comonomer composition on the thermal property of polymer core particle was investigated. By electroless plating method, the nickel particles were formed and deposited on the surface of P(BA-co-Sty) particles to form P(BA-co-Sty) core-nickel shell composite particles. SEM observation confirms that the nickel particles with size of 15 nm are distributed on the surface of the polymer core particles. The surface resistance of P(BA-co-Sty) core-nickel shell composite is 0.8×108Ω/cm2, enough to act as antistatic coating material.展开更多
基金supported by the Korea Research Foundation Grant funded by the Korean Government (MOEHRD,Basic Research Promotion Fund) (KRF-2007-313-D00212)
文摘A transparent and antistatic coating material consisting of polymer core-metal shell particle was prepared. As a polymer core, poly(butylacrylate-co-styrene)s ([P(BA-co-sty)s]) with various compositions of butylacrylate and styrene were synthesized by emulsion polymerization. And the effect of comonomer composition on the thermal property of polymer core particle was investigated. By electroless plating method, the nickel particles were formed and deposited on the surface of P(BA-co-Sty) particles to form P(BA-co-Sty) core-nickel shell composite particles. SEM observation confirms that the nickel particles with size of 15 nm are distributed on the surface of the polymer core particles. The surface resistance of P(BA-co-Sty) core-nickel shell composite is 0.8×108Ω/cm2, enough to act as antistatic coating material.