The cold isostatic press pretreatment process was adopted to prepare fine rare earth oxysulfide up-conversion phosphors with spherical shape, narrow size distribution and high luminescence efficiency. The upconversion...The cold isostatic press pretreatment process was adopted to prepare fine rare earth oxysulfide up-conversion phosphors with spherical shape, narrow size distribution and high luminescence efficiency. The upconversion optical characteristics and brightness of the blue (Y2O2SYb,Tm), green (Y2O2S: Yb,Er), red (Y2O3Yb,Er) emitter were also investigated, and a novel method was successfully developed for the brightness measurement of upconversion luminescence (UPL). It is shown that a white color can be obtained by the appropriate mixture of these primary blue, green and red emissions components. The Er3+ ions exhibit different upconversion mechanism in Y2O2S and Y2O3 host materials. The rare earth oxysulfide is an efficient upconversion matrix. The UPL brightness of Y2O2S: Yb,Er is 6.5 times higher than that of Y2O3: Yb,Er, and Y2O2S: Yb,Er shows UPL brightness of 1100 cd/m2 under 5.56 W/cm2 power density using a 980 nm laser diode.展开更多
基金Supported by the National Natural Science Foundation of China (Grant No.10374011)
文摘The cold isostatic press pretreatment process was adopted to prepare fine rare earth oxysulfide up-conversion phosphors with spherical shape, narrow size distribution and high luminescence efficiency. The upconversion optical characteristics and brightness of the blue (Y2O2SYb,Tm), green (Y2O2S: Yb,Er), red (Y2O3Yb,Er) emitter were also investigated, and a novel method was successfully developed for the brightness measurement of upconversion luminescence (UPL). It is shown that a white color can be obtained by the appropriate mixture of these primary blue, green and red emissions components. The Er3+ ions exhibit different upconversion mechanism in Y2O2S and Y2O3 host materials. The rare earth oxysulfide is an efficient upconversion matrix. The UPL brightness of Y2O2S: Yb,Er is 6.5 times higher than that of Y2O3: Yb,Er, and Y2O2S: Yb,Er shows UPL brightness of 1100 cd/m2 under 5.56 W/cm2 power density using a 980 nm laser diode.