A novel sulfonated polyhedral oligomeric silsesquioxane(S-POSS) monomer was synthesized successfully in this article. S-POSS acted as a donor of sulfonic acid group and reacted with poly(styrene-co-maleic anhydride) (...A novel sulfonated polyhedral oligomeric silsesquioxane(S-POSS) monomer was synthesized successfully in this article. S-POSS acted as a donor of sulfonic acid group and reacted with poly(styrene-co-maleic anhydride) (SMA). FT-IR spectroscopy confirmed the modification through introduction of peaks characteristic of ester linkages and carboxylic groups. The SMA/S-POSS hybrid membranes were fabricated from different S-POSS contents. The proton conductivity and methanol permeability of the hybrid membranes were studied with changing S-POSS content from 5wt.% to 30wt.%. It was found that the proton conductivity and the methanol permeability were dependent on the S-POSS content. Both of proton conductivity and methanol permeability properties improve with increasing S-POSS content. The proton conductivities of the hybrid membranes are in the range of 10-3-10-2 S·cm-1, and the range of methanol permeabilities was between 10-8 and 10-7 cm2·s-1. The membranes show good thermal properties characterized by thermogravimetric analysis (TGA).展开更多
文摘A novel sulfonated polyhedral oligomeric silsesquioxane(S-POSS) monomer was synthesized successfully in this article. S-POSS acted as a donor of sulfonic acid group and reacted with poly(styrene-co-maleic anhydride) (SMA). FT-IR spectroscopy confirmed the modification through introduction of peaks characteristic of ester linkages and carboxylic groups. The SMA/S-POSS hybrid membranes were fabricated from different S-POSS contents. The proton conductivity and methanol permeability of the hybrid membranes were studied with changing S-POSS content from 5wt.% to 30wt.%. It was found that the proton conductivity and the methanol permeability were dependent on the S-POSS content. Both of proton conductivity and methanol permeability properties improve with increasing S-POSS content. The proton conductivities of the hybrid membranes are in the range of 10-3-10-2 S·cm-1, and the range of methanol permeabilities was between 10-8 and 10-7 cm2·s-1. The membranes show good thermal properties characterized by thermogravimetric analysis (TGA).