The 1Cr18Ni9Ti specimens were treated respectively with pulse current under 520 V and 2 600 V during solidification and the solidification structure was observed. The results showed that pulse current can refine solid...The 1Cr18Ni9Ti specimens were treated respectively with pulse current under 520 V and 2 600 V during solidification and the solidification structure was observed. The results showed that pulse current can refine solidification grains, cut primary dentrities remarkably and reduce second dentritic arm spacing. The mechanism and effect are changed with operation parameters.展开更多
By introducing aparameter of difference in ferrite formation temperature between binary Fe-C and multicomponent system,and referring to the thermodynamic model for Fe-C binary system,a simplified thermodynamic model f...By introducing aparameter of difference in ferrite formation temperature between binary Fe-C and multicomponent system,and referring to the thermodynamic model for Fe-C binary system,a simplified thermodynamic model for pro-eutectoid ferrite formation in Fe-ΣXiC multicomponent structural steels(Xi=Mn,Si,Mo,Cr,Ni or Ti,etc)was suggested.The comparison of the calculated Ae3 temperatures with the measured data of steels 42 shows that the relative standard deviation and root-mean-square(RMS)error between them are only 0.71% and 8.92 K,respectively.However,the deviations between the same measured data and the values calculated from the superelement model are as high as 1.86% and 23.83 K,respectively.It can be concluded that the simplified thermodynamic model for pro-eutectoid ferrite formation in multicomponent structural steels is acceptable and the calculated Ae3 temperatures are in good agreement with the experimental data.展开更多
基金Sponsored by National Natural Science Foundation of China(50075053)
文摘The 1Cr18Ni9Ti specimens were treated respectively with pulse current under 520 V and 2 600 V during solidification and the solidification structure was observed. The results showed that pulse current can refine solidification grains, cut primary dentrities remarkably and reduce second dentritic arm spacing. The mechanism and effect are changed with operation parameters.
基金Item Sponsored by National Natural Science Foundation of China(50075053)
文摘By introducing aparameter of difference in ferrite formation temperature between binary Fe-C and multicomponent system,and referring to the thermodynamic model for Fe-C binary system,a simplified thermodynamic model for pro-eutectoid ferrite formation in Fe-ΣXiC multicomponent structural steels(Xi=Mn,Si,Mo,Cr,Ni or Ti,etc)was suggested.The comparison of the calculated Ae3 temperatures with the measured data of steels 42 shows that the relative standard deviation and root-mean-square(RMS)error between them are only 0.71% and 8.92 K,respectively.However,the deviations between the same measured data and the values calculated from the superelement model are as high as 1.86% and 23.83 K,respectively.It can be concluded that the simplified thermodynamic model for pro-eutectoid ferrite formation in multicomponent structural steels is acceptable and the calculated Ae3 temperatures are in good agreement with the experimental data.