Three different kinds of corundum aggregates-tabular sintered alumina, dense sintered alumina, and fused dense corundum-were introduced into the silica fume .free or silica fume containing Al2O3 -SiC - C iron runner c...Three different kinds of corundum aggregates-tabular sintered alumina, dense sintered alumina, and fused dense corundum-were introduced into the silica fume .free or silica fume containing Al2O3 -SiC - C iron runner castables to investigate their influences on the flow ability, linear change on heating, bulk density, apparent porosity, cold strength, hot modulus of rupture, therm, al shock resistance, slag resistance, oxidation resistance as well as wear resistance of Al2O3 - SiC - C iron runner castables. The results show that （ 1 ） compared with the specimens with fused dense corundum, the specimens with dense sintered alumina have equivalent installation property, slag resistance and oxidation resistance, equivalent or even higher cold modulus of rupture, cold crushing strength and hot modulus of rupture, exhibiting better thermal shock resistance and cold wear resistance ; （2） adopting bimodal alumina micropowder LISAL22RABL as well as water reducers ZX2 and ZD2 can well reduce the water requirement of silica fume free castables, solving the problem of deteriorated flow ability resulted from the lack of silica fume; since the lack of silica fume avoids the formation of low melting point liquid, the hot modulus of rupture and the thermal shock resistance of the silica fume free castables are both better than those of the silica fume containing castables ; （3） the density of the castable specimens with dense sintered alumina is 4% -6% lower than that of the castable specimens with Jhsed dense corundum so the refractories consumption of one iron runner reduces by 5% by using the tastable with dense sintered alumina, which obviously reduces the cost of refractories.展开更多
To satisfy the requirements of alumina castables in specific environment and enhance their properties,alumina castables were prepared using tabular alumina,various alumina powders(07RAL,15RA,22RABL,40CA,99-20um,and 99...To satisfy the requirements of alumina castables in specific environment and enhance their properties,alumina castables were prepared using tabular alumina,various alumina powders(07RAL,15RA,22RABL,40CA,99-20um,and 99-325mesh),and calcium aluminate cement as main raw materials,and heat treating at 110,1000,1600℃,respectively.Their flowability and physical properties were tested,and the morphology was researched.The results show that compared with calcined alumina and tabular alumina powders,reactive alumina has higher specific surface area and better filling performance leading to lower water demand and higher viscosity,and the castables prepared with reactive alumina have higher CCS and CMOR after heat treating at 110,1000 and 1600℃as well as lower PLC than those with calcined alumina and tabular alumina powders.展开更多
文摘Three different kinds of corundum aggregates-tabular sintered alumina, dense sintered alumina, and fused dense corundum-were introduced into the silica fume .free or silica fume containing Al2O3 -SiC - C iron runner castables to investigate their influences on the flow ability, linear change on heating, bulk density, apparent porosity, cold strength, hot modulus of rupture, therm, al shock resistance, slag resistance, oxidation resistance as well as wear resistance of Al2O3 - SiC - C iron runner castables. The results show that （ 1 ） compared with the specimens with fused dense corundum, the specimens with dense sintered alumina have equivalent installation property, slag resistance and oxidation resistance, equivalent or even higher cold modulus of rupture, cold crushing strength and hot modulus of rupture, exhibiting better thermal shock resistance and cold wear resistance ; （2） adopting bimodal alumina micropowder LISAL22RABL as well as water reducers ZX2 and ZD2 can well reduce the water requirement of silica fume free castables, solving the problem of deteriorated flow ability resulted from the lack of silica fume; since the lack of silica fume avoids the formation of low melting point liquid, the hot modulus of rupture and the thermal shock resistance of the silica fume free castables are both better than those of the silica fume containing castables ; （3） the density of the castable specimens with dense sintered alumina is 4% -6% lower than that of the castable specimens with Jhsed dense corundum so the refractories consumption of one iron runner reduces by 5% by using the tastable with dense sintered alumina, which obviously reduces the cost of refractories.
文摘To satisfy the requirements of alumina castables in specific environment and enhance their properties,alumina castables were prepared using tabular alumina,various alumina powders(07RAL,15RA,22RABL,40CA,99-20um,and 99-325mesh),and calcium aluminate cement as main raw materials,and heat treating at 110,1000,1600℃,respectively.Their flowability and physical properties were tested,and the morphology was researched.The results show that compared with calcined alumina and tabular alumina powders,reactive alumina has higher specific surface area and better filling performance leading to lower water demand and higher viscosity,and the castables prepared with reactive alumina have higher CCS and CMOR after heat treating at 110,1000 and 1600℃as well as lower PLC than those with calcined alumina and tabular alumina powders.