Silicon aluminum oxynitride (β-Si4Al2O2N6) powder was added into corundum castable and its FeO corrosion resistance was tested in crucible method.It was found that FeO corrosion resistance of sialon containing corund...Silicon aluminum oxynitride (β-Si4Al2O2N6) powder was added into corundum castable and its FeO corrosion resistance was tested in crucible method.It was found that FeO corrosion resistance of sialon containing corundum castables was better than that of no sialon powder added ,The optimum content of the sialon powder in castables was higher than mass of the sialon powder in castables was higher than mass 15%.Moreover,O'-sialon phase,together with β-sialon phase occurred in corundum castables heated in coke bed at 1500℃,although β-sialon powder was initially admixed into the matrix of castables.The EPMA results showed these nitrogen-containing phases located in the matrix of castables were favorable to hinder the penetration of FeO melt at high temperature in comparison with pure corundum castable.However,the flowability of corundum castable became worse originated from the sialon powder added.展开更多
文摘Silicon aluminum oxynitride (β-Si4Al2O2N6) powder was added into corundum castable and its FeO corrosion resistance was tested in crucible method.It was found that FeO corrosion resistance of sialon containing corundum castables was better than that of no sialon powder added ,The optimum content of the sialon powder in castables was higher than mass of the sialon powder in castables was higher than mass 15%.Moreover,O'-sialon phase,together with β-sialon phase occurred in corundum castables heated in coke bed at 1500℃,although β-sialon powder was initially admixed into the matrix of castables.The EPMA results showed these nitrogen-containing phases located in the matrix of castables were favorable to hinder the penetration of FeO melt at high temperature in comparison with pure corundum castable.However,the flowability of corundum castable became worse originated from the sialon powder added.