The present study reports on the growth of calcium phosphate coatings on Ti6Al4V substrate by electrodeposition under high magnetic field.The electrodeposition is conducted by potentiostatic method on horizontal elect...The present study reports on the growth of calcium phosphate coatings on Ti6Al4V substrate by electrodeposition under high magnetic field.The electrodeposition is conducted by potentiostatic method on horizontal electrode whose roughness was modified to reach a value of 3μm.The coatings are obtained from an electrolyte containing calcium nitrate as the Ca^(2+) source and ammonium phosphate as the P source with a Ca/P ratio equal to two.The LNCMI high field continuous magnet in a 170 mm bore with homogeneity of 600.10~6 in I cm^3 has been used.The magnetic field with a magnitude up to 12 T is applied perpendicularly to the electrode surface.The surface morphology and chemical composition of the obtained coatings were characterized by 3D digital microscope and scanning electron microscopy associated with X-ray microanalysis(SEM-EDX).The phase composition was analyzed by X-Ray diffraction.The presence of several crystalline phases comprising octacalcium phosphate and hydroxyapatite is obtained and magnetic field seems to change the relative importance of these phases.The coating morphology changes from belt shape crystallites to needle shape crystallites with high magnetic field superimposition without important modification of Ca/P ratio in the deposit.On the other hand formation of volcano-like structures due to the presence of hydrogen bubbles during deposition is considerably reduced in the presence of magnetic field.展开更多
In this study,the possibility of obtaining micro and nano-scaled Co/Ni bi-layered films by use of the electrochemical method was investigated.The electrodeposition process was performed with presence and absence of a ...In this study,the possibility of obtaining micro and nano-scaled Co/Ni bi-layered films by use of the electrochemical method was investigated.The electrodeposition process was performed with presence and absence of a uniform external magnetic field up to 1T to examine its influence on structure and morphology of the obtained thin films. Afterwards,each sample was annealed under high magnetic field with strength up to 12 T at 623 K,what allowed compare and determine the changes in morphology and structure,before and after heat treatment.The Co/Ni bi-layered thin films were deposited onto an indium-doped tin oxide(ITO)-coated conducting glass substrate from sulfate baths with boric acid as an additive.The results show drastic changes in the morphology between macro and nano-scaled films which were strongly affected by an introduction of the magnetic field to the electrodeposition process.The annealing process allowed to determine the nucleus transition and showed that under the high temperature treatment it is possible to control the growth mode as well as the phase composition changes.展开更多
文摘The present study reports on the growth of calcium phosphate coatings on Ti6Al4V substrate by electrodeposition under high magnetic field.The electrodeposition is conducted by potentiostatic method on horizontal electrode whose roughness was modified to reach a value of 3μm.The coatings are obtained from an electrolyte containing calcium nitrate as the Ca^(2+) source and ammonium phosphate as the P source with a Ca/P ratio equal to two.The LNCMI high field continuous magnet in a 170 mm bore with homogeneity of 600.10~6 in I cm^3 has been used.The magnetic field with a magnitude up to 12 T is applied perpendicularly to the electrode surface.The surface morphology and chemical composition of the obtained coatings were characterized by 3D digital microscope and scanning electron microscopy associated with X-ray microanalysis(SEM-EDX).The phase composition was analyzed by X-Ray diffraction.The presence of several crystalline phases comprising octacalcium phosphate and hydroxyapatite is obtained and magnetic field seems to change the relative importance of these phases.The coating morphology changes from belt shape crystallites to needle shape crystallites with high magnetic field superimposition without important modification of Ca/P ratio in the deposit.On the other hand formation of volcano-like structures due to the presence of hydrogen bubbles during deposition is considerably reduced in the presence of magnetic field.
基金Item Sponsored by National Natural Science Foundation of China(51061130557,51101032)French ANR,Champagne-Ardenne Region Council and Pole MATERALIA(Programme COMAGNET,Grant No.2010-INTB-903-01)
文摘In this study,the possibility of obtaining micro and nano-scaled Co/Ni bi-layered films by use of the electrochemical method was investigated.The electrodeposition process was performed with presence and absence of a uniform external magnetic field up to 1T to examine its influence on structure and morphology of the obtained thin films. Afterwards,each sample was annealed under high magnetic field with strength up to 12 T at 623 K,what allowed compare and determine the changes in morphology and structure,before and after heat treatment.The Co/Ni bi-layered thin films were deposited onto an indium-doped tin oxide(ITO)-coated conducting glass substrate from sulfate baths with boric acid as an additive.The results show drastic changes in the morphology between macro and nano-scaled films which were strongly affected by an introduction of the magnetic field to the electrodeposition process.The annealing process allowed to determine the nucleus transition and showed that under the high temperature treatment it is possible to control the growth mode as well as the phase composition changes.