Monodispersed Ni nanoparticles were successfully prepared by chemical reduction with hydrazine hydrate in ethylene glycol. The effect of the amount of polyvinylpyrrolidone （PVP-K30） on the preparation of Ni nanopart...Monodispersed Ni nanoparticles were successfully prepared by chemical reduction with hydrazine hydrate in ethylene glycol. The effect of the amount of polyvinylpyrrolidone （PVP-K30） on the preparation of Ni nanoparticles was investigated. X-ray diffraction （XRD）, transmission electron microscopy （TEM）, and high resolution transmission electron microscopy （HRTEM） were employed to characterize the nickel powders. The average nickel particle size can be controlled from 103 nm to 46 ran with increasing the mass ratio of PVP to NiCl2·6H2O. The particles are spherical in shape and are not agglomerated. A possible extensive mechanism of nickel nanoparticle formation has been suggested.展开更多
The kinetics of the leaching of carbothermic reduced titanium-bearing blast furnace slag in Panzhihua Iron and Steel Company with acid system under atmosphere pressure was studied. The results show that the temperatur...The kinetics of the leaching of carbothermic reduced titanium-bearing blast furnace slag in Panzhihua Iron and Steel Company with acid system under atmosphere pressure was studied. The results show that the temperature and concentration have significant influence on leaching of carbothermic reduced titanium-bearing blast furnace slag by acid. The experimental data of leaching indicate that the shrinking core model with chemical reaction controlled process is most applicable for the acid leaching. The apparent activation energy can be estimated to be from 23 to 32 k J/mol. Furthermore, the main products are TiC and SiO_2 after leaching.展开更多
文摘Monodispersed Ni nanoparticles were successfully prepared by chemical reduction with hydrazine hydrate in ethylene glycol. The effect of the amount of polyvinylpyrrolidone （PVP-K30） on the preparation of Ni nanoparticles was investigated. X-ray diffraction （XRD）, transmission electron microscopy （TEM）, and high resolution transmission electron microscopy （HRTEM） were employed to characterize the nickel powders. The average nickel particle size can be controlled from 103 nm to 46 ran with increasing the mass ratio of PVP to NiCl2·6H2O. The particles are spherical in shape and are not agglomerated. A possible extensive mechanism of nickel nanoparticle formation has been suggested.
基金Specialized Research Fund for the Doctoral Program of Higher Education (20130006120007)the National Natural Science Foundation of China (51174022, 51304018 and 51474141)
文摘The kinetics of the leaching of carbothermic reduced titanium-bearing blast furnace slag in Panzhihua Iron and Steel Company with acid system under atmosphere pressure was studied. The results show that the temperature and concentration have significant influence on leaching of carbothermic reduced titanium-bearing blast furnace slag by acid. The experimental data of leaching indicate that the shrinking core model with chemical reaction controlled process is most applicable for the acid leaching. The apparent activation energy can be estimated to be from 23 to 32 k J/mol. Furthermore, the main products are TiC and SiO_2 after leaching.