In this paper,the 2.6 vol%TiBw/Ti6Al4V composites with network architecture were fabricated by hot press sintering(HPS)at 1100℃ for 1 h,and the quantitative relationships between phases and heat treatment temperature...In this paper,the 2.6 vol%TiBw/Ti6Al4V composites with network architecture were fabricated by hot press sintering(HPS)at 1100℃ for 1 h,and the quantitative relationships between phases and heat treatment temperatures were established.The results showed that the volume fraction phases changed linearly with a range of solution temperature(930-1010℃)and aging temperature(400-600℃).Moreover,the composites with equiaxed microstructure were obtained due to the static recrystallization after solution treated at 950℃ for 1 h and aging treated at 600℃ for 12 h.The ultimate high temperature tensile strengths were 772,658,392 and 182 MPa,and the elongations were 9.1%,12.5%,28.6%and 35.3%at 400,500,600 and 700℃,respectively.In addition,fractured morphology analysis indicated the excellent strengthening effect of TiBw at a temperature below 600℃.However,the strengthening effect was significantly reduced due to the debonding of matrix and TiBw at 700℃ and caused the cracks to propagate along the grain boundary.展开更多
基金Project(51905123)supported by the National Natural Science Foundation of ChinaProject(ZR2019MEM037)supported by the Natural Science Foundation of Shandong Province,China。
文摘In this paper,the 2.6 vol%TiBw/Ti6Al4V composites with network architecture were fabricated by hot press sintering(HPS)at 1100℃ for 1 h,and the quantitative relationships between phases and heat treatment temperatures were established.The results showed that the volume fraction phases changed linearly with a range of solution temperature(930-1010℃)and aging temperature(400-600℃).Moreover,the composites with equiaxed microstructure were obtained due to the static recrystallization after solution treated at 950℃ for 1 h and aging treated at 600℃ for 12 h.The ultimate high temperature tensile strengths were 772,658,392 and 182 MPa,and the elongations were 9.1%,12.5%,28.6%and 35.3%at 400,500,600 and 700℃,respectively.In addition,fractured morphology analysis indicated the excellent strengthening effect of TiBw at a temperature below 600℃.However,the strengthening effect was significantly reduced due to the debonding of matrix and TiBw at 700℃ and caused the cracks to propagate along the grain boundary.