Bridge steel has been widely used in recent years for its excellent performance. Understanding the high-temperature Dynamic Recrystallization (DRX) behavior of high-performance bridge steel plays an important role in ...Bridge steel has been widely used in recent years for its excellent performance. Understanding the high-temperature Dynamic Recrystallization (DRX) behavior of high-performance bridge steel plays an important role in guiding the thermomechanical processing process. In the present study, the hot deformation behavior of Q370qE bridge steel was investigated by hot compression tests conducted on a Gleeble 3800-GTC thermal-mechanical physical simulation system at temperatures ranging from 900 ℃ to 1100 ℃ and strain rates ranging from 0.01 s^(−1) to 10 s^(−1). The obtained results were used to plot the true stress-strain and work-hardening rate curves of the experimental steel, with the latter curves used to determine the critical strains for the initiation of DRX. The Zener-Hollomon equation was subsequently applied to establish the correspondence between temperature and strain rate during the high-temperature plastic deformation of bridge steel. In terms of the DRX volume fraction solution, a new method for establishing DRX volume fraction was proposed based on two theoretical models. The good weathering and corrosion resistance of bridge steel lead to difculties in microstructure etching. To solve this, the MTEX technology was used to further develop EBSD data to characterize the original microstructure of Q370qE bridge steel. This paper lays the theoretical foundation for studying the DRX behavior of Q370qE bridge steel.展开更多
Centrifugal casting is a foundry process allowing the production of near net-shaped axially symmetrical components. The present study focuses on the microstructural characterization of centrifugally cast alloys featur...Centrifugal casting is a foundry process allowing the production of near net-shaped axially symmetrical components. The present study focuses on the microstructural characterization of centrifugally cast alloys featuring different chemical compositions for the construction of spheres applied in valves made of alloy IN625 for operation at high pressure. Control of the solidification microstructure is needed to assure the reliability of the castings. Actually, a Ni-base superalloy such as this one should have an outstanding combination of mechanical properties, high temperature stability and corrosion resistance. Alloys such as IN625 are characterised by a large amount of alloying elements and a wide solidification range, so they can be affected by micro-porosity defects, related to the shrinkage difference between the matrix and the secondary reinforcing phases(Nb-rich carbides and Laves phase). In this study, the microstructure characterization was performed as a function of the applied heat treatments and it was coupled with a calorimetric analysis in order to understand the mechanism ruling the formation of micro-porosities that can assure alloy soundness. The obtained results show that the presence of micro-porosities is governed by morphology and by the size of the secondary phases, and the presence of the observed secondary phases is detrimental to corrosion resistance.展开更多
A new procedure was proposed for evaluating the weldability of nickel-base superalloys. The theory is on the basis of two microstructural patterns. In pattern I, the weld microstructure exhibits severe alloying segreg...A new procedure was proposed for evaluating the weldability of nickel-base superalloys. The theory is on the basis of two microstructural patterns. In pattern I, the weld microstructure exhibits severe alloying segregation, many low-melting eutectic structures, and low weldability. The weld requires a weaker etchant and a shorter time for etching. In pattern Ⅱ, the weld microstructure displays less alloying segregation, low quantity of eutectic structures, and high weldability. The weld needs a stronger etchant and a longer time for etching. Five superalloys containing different amounts of Nb and Ti were designed to verify the patterns. After welding operations, the welds were etched by four etchants with different corrosivities. The weldability was determined by TG-DSC measurements. The metallography and weldability results confirmed the theoretic patterns. Finally, the etchant corrosivity and etching time were proposed as new criteria to evaluate the weldability of nickel-base superalloys.展开更多
The integrated steelmaking cycle based on the blast furnace-basic oxygen furnace(BOF)route plays an important role in the production of plain and ultra-low carbon steel,especially for deep drawing operations.BOF ste...The integrated steelmaking cycle based on the blast furnace-basic oxygen furnace(BOF)route plays an important role in the production of plain and ultra-low carbon steel,especially for deep drawing operations.BOF steelmaking is based on the conversion of cast iron in steel by impinging oxygen on the metal bath at supersonic speed.In order to avoid the addition of detrimental chemical elements owing to the introduction of uncontrolled scrap and in order to decrease environmental impact caused by the intensive use of coke for the production of cast iron,HBI(hot briquetted iron)can be used as a source of metal and a fraction of cast iron.Forty industrial experimental tests were performed to evaluate the viability of the use of HBI in BOF.The experimental campaign was supported by a thermal prediction model and realized through the estimation of the oxidation enthalpy.Furthermore,the process was thermodynamically analyzed based on oxygen potentials using the off-gas composition and the bath temperature evolution during the conversion as reference data.展开更多
基金Supported by Regional Joint Funds of National Natural Science Foundation of China(Grant No.U20A20289)Hebei Provincial Innovative Research Groups Project of Natural Science Foundation of China(Grant No.E2021203011)+2 种基金General Program of National Natural Science Foundation of China(Grant Nos.52075471,52075473)Hebei Provincial Excellent Youth Science Foundation of China(Grant No.E2021203190)Hebei Provincial Innovative Capacity Cultivation Funding Project for Postgraduates of China(Grant No.CXZZSS2023040).
文摘Bridge steel has been widely used in recent years for its excellent performance. Understanding the high-temperature Dynamic Recrystallization (DRX) behavior of high-performance bridge steel plays an important role in guiding the thermomechanical processing process. In the present study, the hot deformation behavior of Q370qE bridge steel was investigated by hot compression tests conducted on a Gleeble 3800-GTC thermal-mechanical physical simulation system at temperatures ranging from 900 ℃ to 1100 ℃ and strain rates ranging from 0.01 s^(−1) to 10 s^(−1). The obtained results were used to plot the true stress-strain and work-hardening rate curves of the experimental steel, with the latter curves used to determine the critical strains for the initiation of DRX. The Zener-Hollomon equation was subsequently applied to establish the correspondence between temperature and strain rate during the high-temperature plastic deformation of bridge steel. In terms of the DRX volume fraction solution, a new method for establishing DRX volume fraction was proposed based on two theoretical models. The good weathering and corrosion resistance of bridge steel lead to difculties in microstructure etching. To solve this, the MTEX technology was used to further develop EBSD data to characterize the original microstructure of Q370qE bridge steel. This paper lays the theoretical foundation for studying the DRX behavior of Q370qE bridge steel.
文摘Centrifugal casting is a foundry process allowing the production of near net-shaped axially symmetrical components. The present study focuses on the microstructural characterization of centrifugally cast alloys featuring different chemical compositions for the construction of spheres applied in valves made of alloy IN625 for operation at high pressure. Control of the solidification microstructure is needed to assure the reliability of the castings. Actually, a Ni-base superalloy such as this one should have an outstanding combination of mechanical properties, high temperature stability and corrosion resistance. Alloys such as IN625 are characterised by a large amount of alloying elements and a wide solidification range, so they can be affected by micro-porosity defects, related to the shrinkage difference between the matrix and the secondary reinforcing phases(Nb-rich carbides and Laves phase). In this study, the microstructure characterization was performed as a function of the applied heat treatments and it was coupled with a calorimetric analysis in order to understand the mechanism ruling the formation of micro-porosities that can assure alloy soundness. The obtained results show that the presence of micro-porosities is governed by morphology and by the size of the secondary phases, and the presence of the observed secondary phases is detrimental to corrosion resistance.
基金financial support of MAPNA Group under contract No.RD-THD-89-02
文摘A new procedure was proposed for evaluating the weldability of nickel-base superalloys. The theory is on the basis of two microstructural patterns. In pattern I, the weld microstructure exhibits severe alloying segregation, many low-melting eutectic structures, and low weldability. The weld requires a weaker etchant and a shorter time for etching. In pattern Ⅱ, the weld microstructure displays less alloying segregation, low quantity of eutectic structures, and high weldability. The weld needs a stronger etchant and a longer time for etching. Five superalloys containing different amounts of Nb and Ti were designed to verify the patterns. After welding operations, the welds were etched by four etchants with different corrosivities. The weldability was determined by TG-DSC measurements. The metallography and weldability results confirmed the theoretic patterns. Finally, the etchant corrosivity and etching time were proposed as new criteria to evaluate the weldability of nickel-base superalloys.
文摘The integrated steelmaking cycle based on the blast furnace-basic oxygen furnace(BOF)route plays an important role in the production of plain and ultra-low carbon steel,especially for deep drawing operations.BOF steelmaking is based on the conversion of cast iron in steel by impinging oxygen on the metal bath at supersonic speed.In order to avoid the addition of detrimental chemical elements owing to the introduction of uncontrolled scrap and in order to decrease environmental impact caused by the intensive use of coke for the production of cast iron,HBI(hot briquetted iron)can be used as a source of metal and a fraction of cast iron.Forty industrial experimental tests were performed to evaluate the viability of the use of HBI in BOF.The experimental campaign was supported by a thermal prediction model and realized through the estimation of the oxidation enthalpy.Furthermore,the process was thermodynamically analyzed based on oxygen potentials using the off-gas composition and the bath temperature evolution during the conversion as reference data.