Two-dimensional (2D) ultrathin MoS2-modified black Ti^3+-TiO2 nanotubes were fabricated using an electrospinning-hydrothermal treatment-reduction method.Bare TiO2 nanotubes were fabricated via electrospinning.Then,2D ...Two-dimensional (2D) ultrathin MoS2-modified black Ti^3+-TiO2 nanotubes were fabricated using an electrospinning-hydrothermal treatment-reduction method.Bare TiO2 nanotubes were fabricated via electrospinning.Then,2D MoS2 lamellae were grown on the surface of the nanotubes and Ti^3+/Ov ions were introduced by reduction.The photocatalytic performance of the 2D MoS2/Ti^3+-TiO2 nanotubes was^15 times better than that of TiO2.The HER enhancement of the MoS2/Ti^3+-TiO2 nanotubes can be attributed to the Pt-like behavior of 2D MoS2 and the presence of Ti^3+-ions,which facilitated the quick diffusion of the photogenerated electrons to water,reducing the H2 activation barrier.The presence of Ov ions in the nanotubes and their hollow structure increased their solar utilization.展开更多
In this work,polystyrene-based oil-in-water Pickering emulsion stabilized by nanocrystalline cellulose(NCC)was formulated.The NCC was prepared by sulfuric-acid-catalyzed hydrolysis of microcrystalline cellulose,with a...In this work,polystyrene-based oil-in-water Pickering emulsion stabilized by nanocrystalline cellulose(NCC)was formulated.The NCC was prepared by sulfuric-acid-catalyzed hydrolysis of microcrystalline cellulose,with a yield of 60%and an average particle size of about 152.9 nm.When the content of NCC was 5 g/L,the surface tension was 54.58 mN/m,and stable styrene-based Pickering emulsion was prepared using NCC as the stabilizer.The presence of NCC particles in the emulsion system resulted in high resistance against creaming.Due to improved stability,the conversion efficiency of styrene was higher in the polymerization process of the styrene-based Pickering emulsion.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.51672249,51802282,and 11804301)the Zhejiang Provincial Natural Science Foundation of China(Grant Nos.LQ17F040004 and LY17E020001)Fundamental Research Funds of Zhejiang Sci-Tech University(No.2019Q062)。
文摘Two-dimensional (2D) ultrathin MoS2-modified black Ti^3+-TiO2 nanotubes were fabricated using an electrospinning-hydrothermal treatment-reduction method.Bare TiO2 nanotubes were fabricated via electrospinning.Then,2D MoS2 lamellae were grown on the surface of the nanotubes and Ti^3+/Ov ions were introduced by reduction.The photocatalytic performance of the 2D MoS2/Ti^3+-TiO2 nanotubes was^15 times better than that of TiO2.The HER enhancement of the MoS2/Ti^3+-TiO2 nanotubes can be attributed to the Pt-like behavior of 2D MoS2 and the presence of Ti^3+-ions,which facilitated the quick diffusion of the photogenerated electrons to water,reducing the H2 activation barrier.The presence of Ov ions in the nanotubes and their hollow structure increased their solar utilization.
基金Shandong Provincial Natural Science Foundation of China(Grant No.ZR2017MC032)Open Fund of State Key Laboratory Base of Eco-Chemical Engineering(Grant No.KF1706)Undergraduate Training Programs for Innovation and Entrepreneurship at Qingdao University of Science&Technology(201601010).
文摘In this work,polystyrene-based oil-in-water Pickering emulsion stabilized by nanocrystalline cellulose(NCC)was formulated.The NCC was prepared by sulfuric-acid-catalyzed hydrolysis of microcrystalline cellulose,with a yield of 60%and an average particle size of about 152.9 nm.When the content of NCC was 5 g/L,the surface tension was 54.58 mN/m,and stable styrene-based Pickering emulsion was prepared using NCC as the stabilizer.The presence of NCC particles in the emulsion system resulted in high resistance against creaming.Due to improved stability,the conversion efficiency of styrene was higher in the polymerization process of the styrene-based Pickering emulsion.