Hot corrosion behaviors of the 921A alloy and Fe-based amorphous coating induced by KCl-10% ZnCl_(2) and KCl-55% ZnCl_(2) salts at 450℃ in air for 40 h were investigated.Results show that the 921A alloy suffers more ...Hot corrosion behaviors of the 921A alloy and Fe-based amorphous coating induced by KCl-10% ZnCl_(2) and KCl-55% ZnCl_(2) salts at 450℃ in air for 40 h were investigated.Results show that the 921A alloy suffers more serious corrosion damage than the coating and KCl-55% ZnCl_(2) salts are more corrosive than KCl-10% ZnCl_(2) salts.In the two salts,an Fe_(2)O_(3) layer is formed on the 921A alloy surface,while an outer Fe-rich oxide layer and an inner Cr-rich oxide layer are formed on the surface of the coating.Moreover,a certain amount of metal chloride can be found at the oxide/alloy(coating)interface,which can be explained by "active oxidation".However,the corrosion resistance of the Fe-based amorphous coating did not achieve the desired results,probably because the intersplats in the coating serve as corrosion diffusing channels,which facilitate the corrosion damage rate.Nevertheless,the coating is still in amorphous state after hot corrosion exposure.展开更多
基金supported by GuangDong Basic and Applied Basic Research Foundation(No.2020A1515110128).
文摘Hot corrosion behaviors of the 921A alloy and Fe-based amorphous coating induced by KCl-10% ZnCl_(2) and KCl-55% ZnCl_(2) salts at 450℃ in air for 40 h were investigated.Results show that the 921A alloy suffers more serious corrosion damage than the coating and KCl-55% ZnCl_(2) salts are more corrosive than KCl-10% ZnCl_(2) salts.In the two salts,an Fe_(2)O_(3) layer is formed on the 921A alloy surface,while an outer Fe-rich oxide layer and an inner Cr-rich oxide layer are formed on the surface of the coating.Moreover,a certain amount of metal chloride can be found at the oxide/alloy(coating)interface,which can be explained by "active oxidation".However,the corrosion resistance of the Fe-based amorphous coating did not achieve the desired results,probably because the intersplats in the coating serve as corrosion diffusing channels,which facilitate the corrosion damage rate.Nevertheless,the coating is still in amorphous state after hot corrosion exposure.