The emission and the excitation spectra of GdPO4 : Eu^3+ and GdBO3: Eu^3 + prepared by solid state reaction method were investigated using the synchrotron radiation source of SUPERLUMI station of HASYLAB. The ener...The emission and the excitation spectra of GdPO4 : Eu^3+ and GdBO3: Eu^3 + prepared by solid state reaction method were investigated using the synchrotron radiation source of SUPERLUMI station of HASYLAB. The energy transfer between Gd^3+ and Eu^3+ was discussed with the probability of quantum cutting process. In the excitation spectra monitoring the red emission from Eu^3+ , the distinct lines corresponding to the intraconfigurational 4f-4f transitions from Gd^3+ were observed for both samples, indicating an efficient energy transfer from host Gd^3+ ions to the doped Eu^3+ ions. The efficient energy transfer is necessary for the quantum cutting process based on the two-step energy transfer from Gd^3+ to Eu^3+ . However, the overlapping of the lines corresponding to Gd^3+ :^8S7/2→^6GJ and the broad excitation band (180 - 270 nm) due to Eu^3+- O^2- charge transfer states (CTS) around 200 nm cause excitation energy on ^6GJ levels to dissipate into CTS by direct energy transfer, unfavorable to the cross relaxation energy transfer between Gd^3+ and Eu^3+, thus unfavorable to the quantum cutting process. With the help of the general rules governing the energy positions of Eu^3+-O^2- :CTS, the suggestions concerning searching suitable oxide hosts for Gd^3+-Eu^3+ quantum cutting were made.展开更多
At low temperature, some long-lasting phosphors could not work well in practical applications. So it is necessary to investigate the temperature dependence of the phosphors. The Y2O2S.Eu, Ti, Mg microcrystalline sampl...At low temperature, some long-lasting phosphors could not work well in practical applications. So it is necessary to investigate the temperature dependence of the phosphors. The Y2O2S.Eu, Ti, Mg microcrystalline samples were prepared by solid state reaction method. Phosphors were sintered at 1150 ℃ for 20 min in air, putting in and taking out both at high temperature. The emission spectra and the afterglow spectra as well as the thermoluminescence curve were measured for Y2O2S:Eu,展开更多
文摘The emission and the excitation spectra of GdPO4 : Eu^3+ and GdBO3: Eu^3 + prepared by solid state reaction method were investigated using the synchrotron radiation source of SUPERLUMI station of HASYLAB. The energy transfer between Gd^3+ and Eu^3+ was discussed with the probability of quantum cutting process. In the excitation spectra monitoring the red emission from Eu^3+ , the distinct lines corresponding to the intraconfigurational 4f-4f transitions from Gd^3+ were observed for both samples, indicating an efficient energy transfer from host Gd^3+ ions to the doped Eu^3+ ions. The efficient energy transfer is necessary for the quantum cutting process based on the two-step energy transfer from Gd^3+ to Eu^3+ . However, the overlapping of the lines corresponding to Gd^3+ :^8S7/2→^6GJ and the broad excitation band (180 - 270 nm) due to Eu^3+- O^2- charge transfer states (CTS) around 200 nm cause excitation energy on ^6GJ levels to dissipate into CTS by direct energy transfer, unfavorable to the cross relaxation energy transfer between Gd^3+ and Eu^3+, thus unfavorable to the quantum cutting process. With the help of the general rules governing the energy positions of Eu^3+-O^2- :CTS, the suggestions concerning searching suitable oxide hosts for Gd^3+-Eu^3+ quantum cutting were made.
文摘At low temperature, some long-lasting phosphors could not work well in practical applications. So it is necessary to investigate the temperature dependence of the phosphors. The Y2O2S.Eu, Ti, Mg microcrystalline samples were prepared by solid state reaction method. Phosphors were sintered at 1150 ℃ for 20 min in air, putting in and taking out both at high temperature. The emission spectra and the afterglow spectra as well as the thermoluminescence curve were measured for Y2O2S:Eu,