With the expanding application of capacitors,thermal resistant dielectric materials are in high demand due to the increasing harsh environments where the capacitors are needed and the heat generated by the capacitors....With the expanding application of capacitors,thermal resistant dielectric materials are in high demand due to the increasing harsh environments where the capacitors are needed and the heat generated by the capacitors.Herein,we present polyarylene ether nitrile and titanium dioxide hybrids which can be used as thermal resistant dielectrics for these capacitors.Phthalonitrile modified titanium dioxide(TiO_(2)-CN)and phthalonitrile end-capped polyarylene ether nitrile(PEN-Ph)are firstly prepared.After being cast into TiO_(2)-CN/PEN nanocomposite films,these composites self-crosslink upon heating at 320℃for 4 h,forming the polyarylene ether nitrile and titanium dioxide hybrids(TiO_(2)-PEN).Improved dielectric constants which are stable from room temperature to 200℃of these hybrids are observed,indicating the potential application of the hybrids as thermal resistant dielectrics.展开更多
High-quality film capacitors are widely used in many fields such as new energy vehicles,electronic communications,etc.,due to their advantages in wide frequency response and low dielectric loss.The dielectric film is ...High-quality film capacitors are widely used in many fields such as new energy vehicles,electronic communications,etc.,due to their advantages in wide frequency response and low dielectric loss.The dielectric film is a crucial part of the film capacitor,and its properties have an important impact on the performance and use conditions of the film capacitor.In this work,a novel high-temperature-resistant dielectric film was prepared.Firstly,the Bi_(2)S_(3)/rGO-CN fillers were prepared by hydrothermal method combined with cyanation treatment,and then added to the poly(arylene ether nitrile)(PEN)matrix to prepare the dielectric film materials(PEN/Bi_(2)S_(3)/rGO-CN).After high temperature treatment,the fillers Bi_(2)S_(3)/rGO-CN reacted with the PEN matrix,and the composites materials transformed into a thermosetting hybrid film(PEN-Bi_(2)S_(3)/rGO)with gel content of 97.88%.The prepared hybrid dielectric films did not decompose significantly before 400℃,and showed a glass transition temperature(Tg)of up to 252.4℃,which could increase the effective use temperature of the materials.Compared with the composite films without heat treatment,they exhibit better mechanical properties,with further improvement in tensile strength and elastic modulus,and a decrease in elongation at break.The dielectric constant of the hybrid films can be up to 6.8 while the dielectric loss is only about 0.02 at 1 kHz.Moreover,the hybrid films showed excellent dielectric stability during temperature changes,and remain relatively stable before 250℃,which is suitable as a high-temperature-resistant high-dielectric material and is more advantageous for practical applications.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51773028)。
文摘With the expanding application of capacitors,thermal resistant dielectric materials are in high demand due to the increasing harsh environments where the capacitors are needed and the heat generated by the capacitors.Herein,we present polyarylene ether nitrile and titanium dioxide hybrids which can be used as thermal resistant dielectrics for these capacitors.Phthalonitrile modified titanium dioxide(TiO_(2)-CN)and phthalonitrile end-capped polyarylene ether nitrile(PEN-Ph)are firstly prepared.After being cast into TiO_(2)-CN/PEN nanocomposite films,these composites self-crosslink upon heating at 320℃for 4 h,forming the polyarylene ether nitrile and titanium dioxide hybrids(TiO_(2)-PEN).Improved dielectric constants which are stable from room temperature to 200℃of these hybrids are observed,indicating the potential application of the hybrids as thermal resistant dielectrics.
基金financially supported by the National Natural Science Foundation of China(Nos.52073039,51903029,21805027,51803020 and 51773028)International Science and Technology Cooperation Project(No.52011530027)+3 种基金Major Special Projects of Sichuan Province(Nos.2020YFG0270,2020ZDZX0020,2019ZDZX0027 and 2019ZDZX0016)the Fundamental Research Funds for the Central Universities(No.ZYGX2019J026)Sichuan Science and Technology Program(Nos.2019YJ0197,2019YFG0056 and 2020YFG0100)International Science and Technology Cooperation Project from Chengdu municipal government(No.2019-GH02-00037-HZ)。
文摘High-quality film capacitors are widely used in many fields such as new energy vehicles,electronic communications,etc.,due to their advantages in wide frequency response and low dielectric loss.The dielectric film is a crucial part of the film capacitor,and its properties have an important impact on the performance and use conditions of the film capacitor.In this work,a novel high-temperature-resistant dielectric film was prepared.Firstly,the Bi_(2)S_(3)/rGO-CN fillers were prepared by hydrothermal method combined with cyanation treatment,and then added to the poly(arylene ether nitrile)(PEN)matrix to prepare the dielectric film materials(PEN/Bi_(2)S_(3)/rGO-CN).After high temperature treatment,the fillers Bi_(2)S_(3)/rGO-CN reacted with the PEN matrix,and the composites materials transformed into a thermosetting hybrid film(PEN-Bi_(2)S_(3)/rGO)with gel content of 97.88%.The prepared hybrid dielectric films did not decompose significantly before 400℃,and showed a glass transition temperature(Tg)of up to 252.4℃,which could increase the effective use temperature of the materials.Compared with the composite films without heat treatment,they exhibit better mechanical properties,with further improvement in tensile strength and elastic modulus,and a decrease in elongation at break.The dielectric constant of the hybrid films can be up to 6.8 while the dielectric loss is only about 0.02 at 1 kHz.Moreover,the hybrid films showed excellent dielectric stability during temperature changes,and remain relatively stable before 250℃,which is suitable as a high-temperature-resistant high-dielectric material and is more advantageous for practical applications.