This study selected water-cement ratio 0.5 and slump 16 cm for ACI mix design, and used nano- clay to replace 0.1%, 0.3% and 0.5% of cement by weight to make cylinder and angle column specimens. The effects of differe...This study selected water-cement ratio 0.5 and slump 16 cm for ACI mix design, and used nano- clay to replace 0.1%, 0.3% and 0.5% of cement by weight to make cylinder and angle column specimens. The effects of different high temperatures on the compressive strength and heat transfer coefficient were tested, and the ignition loss of nano-clay cement paste was measured. The results showed that an appropriate replacement of nano-clay for 0.3% - 0.5% of cement can enhance the strength and heat transfer coefficient of concrete, especially 0.3% replacement. The 0.1% nano- clay replacement for cement reduces the strength and heat transfer coefficient of concrete. When the ambient temperature exceeds 300?C, the nano-clay concrete strength begins to decline, and the heat transfer coefficient decreases greatly, the effect of hot environment on the strength trend of nano-clay concrete is similar to that on normal concrete. When the nano-clay replaces cement by 0% - 0.5%, the ignition loss is approximately in exponential and logarithmic relationships to the compressive strength respectively when the ignition loss is smaller than and greater than 6%.展开更多
文摘This study selected water-cement ratio 0.5 and slump 16 cm for ACI mix design, and used nano- clay to replace 0.1%, 0.3% and 0.5% of cement by weight to make cylinder and angle column specimens. The effects of different high temperatures on the compressive strength and heat transfer coefficient were tested, and the ignition loss of nano-clay cement paste was measured. The results showed that an appropriate replacement of nano-clay for 0.3% - 0.5% of cement can enhance the strength and heat transfer coefficient of concrete, especially 0.3% replacement. The 0.1% nano- clay replacement for cement reduces the strength and heat transfer coefficient of concrete. When the ambient temperature exceeds 300?C, the nano-clay concrete strength begins to decline, and the heat transfer coefficient decreases greatly, the effect of hot environment on the strength trend of nano-clay concrete is similar to that on normal concrete. When the nano-clay replaces cement by 0% - 0.5%, the ignition loss is approximately in exponential and logarithmic relationships to the compressive strength respectively when the ignition loss is smaller than and greater than 6%.