In order to confirm the optimal Li content of Li-rich Mn-based cathode materials(a fixed mole ratio of Mn to Ni to Co is0.6:0.2:0.2),Li1+x(Mn0.6Ni0.2Co0.2)1-xO2(x=0,0.1,0.2,0.3)composites were obtained,which had a typ...In order to confirm the optimal Li content of Li-rich Mn-based cathode materials(a fixed mole ratio of Mn to Ni to Co is0.6:0.2:0.2),Li1+x(Mn0.6Ni0.2Co0.2)1-xO2(x=0,0.1,0.2,0.3)composites were obtained,which had a typical layered structure with R3m and C2/m space group observed from X-ray powder diffraction(XRD).Electron microscopy micrograph(SEM)reveals that the particle sizes in the range of0.4-1.1μm increase with an increase of x value.Li1.2(Mn0.6Ni0.2Co0.2)0.8O2sample delivers a larger initial discharge capacity of275.7mA·h/g at the current density of20mA/g in the potential range of2.0-4.8V,while Li1.1(Mn0.6Ni0.2Co0.2)0.9O2shows a better cycle performance with a capacity retention of93.8%at0.2C after50cycles,showing better reaction kinetics of lithium ion insertion and extraction.展开更多
基金Project(21473258) supported by the National Natural Science Foundation of ChinaProject(13JJ1004) supported by Distinguished Young Scientists of Hunan Province,ChinaProject(NCET-11-0513) supported by Program for the New Century Excellent Talents in University,China
文摘In order to confirm the optimal Li content of Li-rich Mn-based cathode materials(a fixed mole ratio of Mn to Ni to Co is0.6:0.2:0.2),Li1+x(Mn0.6Ni0.2Co0.2)1-xO2(x=0,0.1,0.2,0.3)composites were obtained,which had a typical layered structure with R3m and C2/m space group observed from X-ray powder diffraction(XRD).Electron microscopy micrograph(SEM)reveals that the particle sizes in the range of0.4-1.1μm increase with an increase of x value.Li1.2(Mn0.6Ni0.2Co0.2)0.8O2sample delivers a larger initial discharge capacity of275.7mA·h/g at the current density of20mA/g in the potential range of2.0-4.8V,while Li1.1(Mn0.6Ni0.2Co0.2)0.9O2shows a better cycle performance with a capacity retention of93.8%at0.2C after50cycles,showing better reaction kinetics of lithium ion insertion and extraction.