The CO_2 sensing of PrFeO_3 and NdFeO_3 sensors were investigated. Experimental results show that the resistances for PrFeO_3 and NdFeO_3 in CO_2 gas are larger than those in air and the responses for PrFeO_3and NdFeO...The CO_2 sensing of PrFeO_3 and NdFeO_3 sensors were investigated. Experimental results show that the resistances for PrFeO_3 and NdFeO_3 in CO_2 gas are larger than those in air and the responses for PrFeO_3and NdFeO_3 sensors increase with an increase in room-temperature relative humidity. When exposed to1000 ppm CO_2, the response of PrFeO_3 thick film based on nano-powders annealed at 700℃can reach8.44 at 160℃for the background of wet air with 58%of room-temperature relative humidity (RH),which is much larger than the corresponding value (3.03) in wet air with 25%RH. The sensing response S of NdFeO_3 thick-film sensor based on nano-powders annealed at 600℃to 3000 ppm CO_2 at the operating temperature 200℃can reach 2.36 for the background of wet air with 72%RH, which is larger than the corresponding value (1.83) in the air with 25%RH. Compared with other CO_2 sensing materials, the PrFeO_3 sensor has larger response at lower operating temperature for CO_2 gas and may be used as a new CO_2 sensing material.展开更多
基金supported by National Natural Science Foundation of China(51272133,51472145,51772174 and 51472150)Shandong Natural Science Foundation(ZR2016EMM20)
文摘The CO_2 sensing of PrFeO_3 and NdFeO_3 sensors were investigated. Experimental results show that the resistances for PrFeO_3 and NdFeO_3 in CO_2 gas are larger than those in air and the responses for PrFeO_3and NdFeO_3 sensors increase with an increase in room-temperature relative humidity. When exposed to1000 ppm CO_2, the response of PrFeO_3 thick film based on nano-powders annealed at 700℃can reach8.44 at 160℃for the background of wet air with 58%of room-temperature relative humidity (RH),which is much larger than the corresponding value (3.03) in wet air with 25%RH. The sensing response S of NdFeO_3 thick-film sensor based on nano-powders annealed at 600℃to 3000 ppm CO_2 at the operating temperature 200℃can reach 2.36 for the background of wet air with 72%RH, which is larger than the corresponding value (1.83) in the air with 25%RH. Compared with other CO_2 sensing materials, the PrFeO_3 sensor has larger response at lower operating temperature for CO_2 gas and may be used as a new CO_2 sensing material.