Blast response of clay brick masonry unit walls unreinforced and reinforced with polyurea elastomer

Clay brick masonry unit(CBMU) walls are widely used in building structures,and its damage and protection under explosion loads have been a matter of concern in the field of engineering protection.In this paper,a series of full-scale experiments of the response characteristics of 24 cm CMBU walls unreinforced and reinforced with polyurea elastomer subjected to blast loading were carried out.Through setting 5.0 kg TNT charges at different stand-off distances,the damage characteristics of masonry walls at different scaled distances were obtained.The reinforcement effect of different polyurea coating thicknesses and methods on the blast resistance performance of masonry walls under single and repeated loads were also explored.Five failure grades were summarized according to the dynamic response features of masonry walls.Based on the stress wave propagation pattern in multi-media composite structures,the internal stress distribution of masonry walls were analyzed,and the division basis of the masonry walls’ failure grades was then quantified.Combined with Scanning Electron Microscope(SEM)images,the deformation characteristics of soft and hard segments of polyurea and effects of detonation products on microstructures were revealed respectively,which provides an important reference for the design and application of polyurea in the blast resistance of clay brick masonry walls.

Experimental investigation on anti-penetration performance of polyurea-coated ASTM1045 steel plate subjected to projectile impact

In this study,the anti-penetration performance of polyurea/ASTM1405-steel composite plate subjected to high velocity projectile was analyzed.Two kinds of modified polyurea material(AMMT-053 and AMMT-055)were selected and a ballistic impact testing system including speed measuring target system and high-speed camera was designed.This experiment was conducted with a rifle and 5.8 mm projectile to explore the effects by the polyurea coating thickness,the polyurea coating position and the glass-fiber cloth on the anti-penetration performance of polyurea/ASTM1405-steel composite plate.The result showed that the effects of polyurea coating position were different between two types of polyurea,and that the effects of glass-fiber position were disparate between two types of polyurea as well.For AMMT-053 polyurea material,it was better to be on front face than on rear face;whereas for AMMT-055 polyurea,it was better to be on rear surface although the difference was very subtle.Additionally,formulas had been given to describe the relationship between the effectiveness of polyurea and the thickness of polyurea coating.In general,AMMT-055 had better anti-penetration performance than AMMT-053.Furthermore,five typical damage modes including self-healing,crack,local bulge,spallation and local fragmentation were defined and the failure mechanism was analyzed with the results of SHPB test.Additionally,the bonding strength played an important role in the anti-penetration performance of polyurea/steel composite plate.