An environmental friendly carbonaceous material- carboresP （one of the Carbores series materials） was investigated for the production of MgO-C refractories in laboratory scale and field tests. The MgO-C specimens we...An environmental friendly carbonaceous material- carboresP （one of the Carbores series materials） was investigated for the production of MgO-C refractories in laboratory scale and field tests. The MgO-C specimens were produced with different CarboresP contents. The bulk density （180℃ × 48h）, CCS, apparent porosity （1000℃ ×3h ） and hot modulus of rupture （1400℃ ×0. 5h ） were tested and contrasted. The appropriate amount of carboresP was 1.0%. The amount of metallic additions can be partially substituted （reduced to 1.5% ）. The microstructure of resin-carboresP binder is anisotropic structure with high oxidation resistance and good thermal-shock stability. The Stress/strain curve indicates that the characteristic length, （LCH） of MgO-C brick with resin/CarboresP bonding has been improved, which means the MgO-C bricks have good mechanical flexibility and stresses absorbability. Field tests were done in slag line of a 40t LF-VD refining steel ladle using Resin/CarboresP bonded ＂ MT-14A MgO-C bricks. The result shows that the MgO-C bricks by ＂soft bonding＂ have good physical properties and excellent workability during production of the bricks . In contrast with traditional MgO-C brick used for secondary refining furnaces, the spalling tendency of the bricks could be reduced significantly. The average lining life of the resin/ CarboresP bricks has increased by 18. 4% comparing with the pure resin-bonded types.展开更多
文摘An environmental friendly carbonaceous material- carboresP （one of the Carbores series materials） was investigated for the production of MgO-C refractories in laboratory scale and field tests. The MgO-C specimens were produced with different CarboresP contents. The bulk density （180℃ × 48h）, CCS, apparent porosity （1000℃ ×3h ） and hot modulus of rupture （1400℃ ×0. 5h ） were tested and contrasted. The appropriate amount of carboresP was 1.0%. The amount of metallic additions can be partially substituted （reduced to 1.5% ）. The microstructure of resin-carboresP binder is anisotropic structure with high oxidation resistance and good thermal-shock stability. The Stress/strain curve indicates that the characteristic length, （LCH） of MgO-C brick with resin/CarboresP bonding has been improved, which means the MgO-C bricks have good mechanical flexibility and stresses absorbability. Field tests were done in slag line of a 40t LF-VD refining steel ladle using Resin/CarboresP bonded ＂ MT-14A MgO-C bricks. The result shows that the MgO-C bricks by ＂soft bonding＂ have good physical properties and excellent workability during production of the bricks . In contrast with traditional MgO-C brick used for secondary refining furnaces, the spalling tendency of the bricks could be reduced significantly. The average lining life of the resin/ CarboresP bricks has increased by 18. 4% comparing with the pure resin-bonded types.