Regularity of the initial atmospheric corrosion of A3 steel in the presence of NaCI was investigated. The results showed that NaCI can accelerate the corrosion of A3 steel. Dry mass gain of A3 steel in the presence of...Regularity of the initial atmospheric corrosion of A3 steel in the presence of NaCI was investigated. The results showed that NaCI can accelerate the corrosion of A3 steel. Dry mass gain of A3 steel in the presence of NaCI deposition increases with the exposure time, which can be correlated by using exponential decay function. The relationship between dry mass gain and amount of NaCI deposition at a certain exposure time follows a quadratic function. More amount of NaCI deposition will slow down the corrosion rate to some extent after exposure for a certain time. SEM/EDAX was used to characterize the corrosion surface and products. The surfaces of the NaCI treated A3 steel were obviously uneven, and some tiny crevices appear in the corrosion products that could help O2 transmit to the inner layer. The amount of oxygen in atomic percentage in the corrosion products increases with the amount of NaCI deposition.展开更多
A laboratory study of the atmospheric corrosion of carbon steel deposited with (NH4)2SO4 in the presence of SO2 is reported. The different levels of (NH4)2SO4 (0, 15, 30, 45, 60 μg·cm-2) were added on the surfac...A laboratory study of the atmospheric corrosion of carbon steel deposited with (NH4)2SO4 in the presence of SO2 is reported. The different levels of (NH4)2SO4 (0, 15, 30, 45, 60 μg·cm-2) were added on the surface of the samples before the exposure. The corrosion was investigated by a combination of gravimetry, Fourier transform infrared spectroscope and scanning electron microscopy. A detailed knowledge about the corrosion products was acquired, both quantitatively and qualitatively. The results show that the metal loss increased and the increasing tendency of corrosion rates slowed down with the increasing exposure time. The phase constituents of the corrosion products are mainly α-FeO(OH), γ-FeO(OH), and δ-FeO(OH).展开更多
Technological process of rare earth sealing anodized LY12 (2024) alloy is introduced. Corrosion behavior of the film was studied by polarization curves and electrochemical impedance spectroscopy (EIS). The results sho...Technological process of rare earth sealing anodized LY12 (2024) alloy is introduced. Corrosion behavior of the film was studied by polarization curves and electrochemical impedance spectroscopy (EIS). The results showed that the coating remained passivity at the potential range from the open circuit potential (-780 mV) to -250 mV in NaCl solution. When the potential exceeded -200 mV, corrosion reaction happened on the coating, the results of EIS analysis was consistent with the results of polarization curves.展开更多
A method of concentration analysis based on X-ray photoelectron spectroscopy (XPS) results was introduced. The concentration of Ce-rich conversion coating on the anodized Al based metal matrix composites AI6061/SiCp w...A method of concentration analysis based on X-ray photoelectron spectroscopy (XPS) results was introduced. The concentration of Ce-rich conversion coating on the anodized Al based metal matrix composites AI6061/SiCp was then studied according to this method. The results revealed that the Ce conversion coating on the anodized AI6061/SiCp consisted of Al oxide, Ce oxide and Ce hydroxide. The state of Ce element exhibited the mixture of Ce3+ and Ce4+. Some of Cell I was oxidized to be CelV in the outer layer coating.展开更多
基金This work was financially supported by the National Natural Science Foundation of China. The number of the project is 5989914. The authors are grateful to Ms. Ping Wan for English diction.
文摘Regularity of the initial atmospheric corrosion of A3 steel in the presence of NaCI was investigated. The results showed that NaCI can accelerate the corrosion of A3 steel. Dry mass gain of A3 steel in the presence of NaCI deposition increases with the exposure time, which can be correlated by using exponential decay function. The relationship between dry mass gain and amount of NaCI deposition at a certain exposure time follows a quadratic function. More amount of NaCI deposition will slow down the corrosion rate to some extent after exposure for a certain time. SEM/EDAX was used to characterize the corrosion surface and products. The surfaces of the NaCI treated A3 steel were obviously uneven, and some tiny crevices appear in the corrosion products that could help O2 transmit to the inner layer. The amount of oxygen in atomic percentage in the corrosion products increases with the amount of NaCI deposition.
文摘A laboratory study of the atmospheric corrosion of carbon steel deposited with (NH4)2SO4 in the presence of SO2 is reported. The different levels of (NH4)2SO4 (0, 15, 30, 45, 60 μg·cm-2) were added on the surface of the samples before the exposure. The corrosion was investigated by a combination of gravimetry, Fourier transform infrared spectroscope and scanning electron microscopy. A detailed knowledge about the corrosion products was acquired, both quantitatively and qualitatively. The results show that the metal loss increased and the increasing tendency of corrosion rates slowed down with the increasing exposure time. The phase constituents of the corrosion products are mainly α-FeO(OH), γ-FeO(OH), and δ-FeO(OH).
基金This work has been carried out with the support of The Chinese Postdoctoral Science FundThe Special Funds for the Major State Basic Research Projects G19990650.
基金This work has been carried out with the support of the Chinese Postdoctoral Science Fund and the Special Funds for the Major State Basic Research Projects G19990650.
文摘Technological process of rare earth sealing anodized LY12 (2024) alloy is introduced. Corrosion behavior of the film was studied by polarization curves and electrochemical impedance spectroscopy (EIS). The results showed that the coating remained passivity at the potential range from the open circuit potential (-780 mV) to -250 mV in NaCl solution. When the potential exceeded -200 mV, corrosion reaction happened on the coating, the results of EIS analysis was consistent with the results of polarization curves.
基金This work has been carried out with the support of The Chinese Postdoctoral Science Fund and The Special Funds for the Major State Basic Research Projects G19990650.
文摘A method of concentration analysis based on X-ray photoelectron spectroscopy (XPS) results was introduced. The concentration of Ce-rich conversion coating on the anodized Al based metal matrix composites AI6061/SiCp was then studied according to this method. The results revealed that the Ce conversion coating on the anodized AI6061/SiCp consisted of Al oxide, Ce oxide and Ce hydroxide. The state of Ce element exhibited the mixture of Ce3+ and Ce4+. Some of Cell I was oxidized to be CelV in the outer layer coating.