Effect of Mg addition on the compositions of inclusions were studied. The results show that Mg can minimize the inclusions of steel obviously. Under the present condition, Mg deoxidation products of low-S content expe...Effect of Mg addition on the compositions of inclusions were studied. The results show that Mg can minimize the inclusions of steel obviously. Under the present condition, Mg deoxidation products of low-S content experimental steel would be changed in the order of Al2O3→MgAl2O4→Mg–Al–O–S→Mg–O–S. Mg deoxidation products of high-S content experimental steel generate Mg–S(–O)+MnS type inclusions, except for usual oxysulfide. And it is consistent with the results of thermodynamics calculation. Mg is preferred to react with oxide, compared with sulfide. The reaction reaches the equilibrium after 1 min or 5 min. It shows that the number and diameter of inclusions in all experimental steel samples are well under control, helping to improve the properties of steel.展开更多
There are four types of Mg–Al–Si–O inclusions observed in the Mg-treated Al-deoxidized ultra-low-carbon steel con-taining trace Si,including SiO_(2),2MgO·SiO_(2),3Al_(2)O_(3)·2SiO_(2),and 2MgO·Al_(2)...There are four types of Mg–Al–Si–O inclusions observed in the Mg-treated Al-deoxidized ultra-low-carbon steel con-taining trace Si,including SiO_(2),2MgO·SiO_(2),3Al_(2)O_(3)·2SiO_(2),and 2MgO·Al_(2)O_(3)·5SiO_(2)and their composite inclusions.Using FactSage,the phase relationship of Mg–Al–Si–O system at 1473–2073 K was calculated using FactSage software,and the change in Si content can change the stable region range of different Mg–Al–Si–O-based inclusions.Based on the types of inclusions observed experimentally,the formation pathways of inclusions were predicted and a kinetic model was established to describe the formation process of the xMgO·yAl_(2)O_(3)–Mg–Al–Si–O and xAl_(2)O_(3)·ySiO_(2)–Mg–Al–Si–O inclusions.展开更多
基金Item Sponsored by National Natural Science Foundation of China(50904017)Fundamental Research Funds for the Central Universities of China(N120502004,N120602005)
文摘Effect of Mg addition on the compositions of inclusions were studied. The results show that Mg can minimize the inclusions of steel obviously. Under the present condition, Mg deoxidation products of low-S content experimental steel would be changed in the order of Al2O3→MgAl2O4→Mg–Al–O–S→Mg–O–S. Mg deoxidation products of high-S content experimental steel generate Mg–S(–O)+MnS type inclusions, except for usual oxysulfide. And it is consistent with the results of thermodynamics calculation. Mg is preferred to react with oxide, compared with sulfide. The reaction reaches the equilibrium after 1 min or 5 min. It shows that the number and diameter of inclusions in all experimental steel samples are well under control, helping to improve the properties of steel.
基金The authors are grateful to the National Natural Science Foundation of China(Grant No.51874170)the Union Foundation of State Key Laboratory of Marine Equipment and Applications-University of Science and Technology Liaoning(SKLMEA-USTL-201706)for supporting this work.
文摘There are four types of Mg–Al–Si–O inclusions observed in the Mg-treated Al-deoxidized ultra-low-carbon steel con-taining trace Si,including SiO_(2),2MgO·SiO_(2),3Al_(2)O_(3)·2SiO_(2),and 2MgO·Al_(2)O_(3)·5SiO_(2)and their composite inclusions.Using FactSage,the phase relationship of Mg–Al–Si–O system at 1473–2073 K was calculated using FactSage software,and the change in Si content can change the stable region range of different Mg–Al–Si–O-based inclusions.Based on the types of inclusions observed experimentally,the formation pathways of inclusions were predicted and a kinetic model was established to describe the formation process of the xMgO·yAl_(2)O_(3)–Mg–Al–Si–O and xAl_(2)O_(3)·ySiO_(2)–Mg–Al–Si–O inclusions.