A novel white light emitting long-lasting phosphor Cd1-xDyxSiO3 is reported in this letter. The Dy3+ doped CdSiO3 phosphor emits white light. The phosphorescence can be seen with the naked eye in the dark clearly ev...A novel white light emitting long-lasting phosphor Cd1-xDyxSiO3 is reported in this letter. The Dy3+ doped CdSiO3 phosphor emits white light. The phosphorescence can be seen with the naked eye in the dark clearly even after the 254 nm UV irradiation have been removed for about 30 min. In the emission spectrum of 5% Dy3+ doped CdSiO3 phosphor, there are two emission peaks of Dy3+, 580 nm (4F9/26H13/2) and 486 nm (4F9/26H15/2), as well as a broad band emission located at about 410 nm. All the three emissions form a white light with CIE chromaticity coordinates x=0.3874, y=0.3760 and the color temperature is 4000 K under 254 nm excitation. It indicated that this phosphor is a promising new luminescent material for practice application.展开更多
Barium lithium fluoride nanocrystals were synthesized in cetyltrimethylammonium bromide (CTAB)/ 2-octanol/ water microemulsion systems. The impurity peaks in XRD patterns were not determined. The result of SEM confi...Barium lithium fluoride nanocrystals were synthesized in cetyltrimethylammonium bromide (CTAB)/ 2-octanol/ water microemulsion systems. The impurity peaks in XRD patterns were not determined. The result of SEM confirmed that the average sizes and shape of the BaLiF3 nanocrystals. The formation of BaLiF3 and particles size were strongly affected by water content. With increasing water content and reaction times, the size of the particle increases. Meanwhile, the solvent was also found to play a key role in the synthesis of the BaLiF3 nanocrystals.展开更多
文摘A novel white light emitting long-lasting phosphor Cd1-xDyxSiO3 is reported in this letter. The Dy3+ doped CdSiO3 phosphor emits white light. The phosphorescence can be seen with the naked eye in the dark clearly even after the 254 nm UV irradiation have been removed for about 30 min. In the emission spectrum of 5% Dy3+ doped CdSiO3 phosphor, there are two emission peaks of Dy3+, 580 nm (4F9/26H13/2) and 486 nm (4F9/26H15/2), as well as a broad band emission located at about 410 nm. All the three emissions form a white light with CIE chromaticity coordinates x=0.3874, y=0.3760 and the color temperature is 4000 K under 254 nm excitation. It indicated that this phosphor is a promising new luminescent material for practice application.
文摘Barium lithium fluoride nanocrystals were synthesized in cetyltrimethylammonium bromide (CTAB)/ 2-octanol/ water microemulsion systems. The impurity peaks in XRD patterns were not determined. The result of SEM confirmed that the average sizes and shape of the BaLiF3 nanocrystals. The formation of BaLiF3 and particles size were strongly affected by water content. With increasing water content and reaction times, the size of the particle increases. Meanwhile, the solvent was also found to play a key role in the synthesis of the BaLiF3 nanocrystals.