The fatigue life of numerous aerospace,locomotive,automotive and biomedical structures may go beyond 10~8 cycles.Determination of long life fatigue behavior becomes extremely important for better understanding and des...The fatigue life of numerous aerospace,locomotive,automotive and biomedical structures may go beyond 10~8 cycles.Determination of long life fatigue behavior becomes extremely important for better understanding and design of the components and structures.Initially,before the invention of ultrasonic fatigue testing,most of the engineering materials were supposed to exhibit fatigue life up to 10~7 cycles or less.This paper reviews current understanding of some fundamental aspects on the development of accelerated fatigue testing method and its application in ultra-high cycle fatigue,crack initiation and growth mechanisms of internal fracture,S-N diagram,fatigue limit and life prediction, etc.展开更多
Carbon-manganese steel is often applied in components of pipes in nuclear plant. Ultrasonic fatigue tests following low cycle fatigue （LCF） cycles damaged are used to study the strength of very high cycle fatigure ...Carbon-manganese steel is often applied in components of pipes in nuclear plant. Ultrasonic fatigue tests following low cycle fatigue （LCF） cycles damaged are used to study the strength of very high cycle fatigure （VHCF）. The comparison of test results of simple VHCF and cumulative fatigue （LCF plus VHCF） shows that LCF load influences the following VHCF strength. Continuum damage mechanics model is extended to VHCF region.展开更多
基金supported by the National Natural Science Foundation of China(10925211)the Program for Changjiang Scholars and Innovative Research Team (IRT1027)
文摘The fatigue life of numerous aerospace,locomotive,automotive and biomedical structures may go beyond 10~8 cycles.Determination of long life fatigue behavior becomes extremely important for better understanding and design of the components and structures.Initially,before the invention of ultrasonic fatigue testing,most of the engineering materials were supposed to exhibit fatigue life up to 10~7 cycles or less.This paper reviews current understanding of some fundamental aspects on the development of accelerated fatigue testing method and its application in ultra-high cycle fatigue,crack initiation and growth mechanisms of internal fracture,S-N diagram,fatigue limit and life prediction, etc.
基金supported by AREVA(France)the National Natural Science Foundation of China(51101107)
文摘Carbon-manganese steel is often applied in components of pipes in nuclear plant. Ultrasonic fatigue tests following low cycle fatigue （LCF） cycles damaged are used to study the strength of very high cycle fatigure （VHCF）. The comparison of test results of simple VHCF and cumulative fatigue （LCF plus VHCF） shows that LCF load influences the following VHCF strength. Continuum damage mechanics model is extended to VHCF region.