A Re-containing Ni-base single crystal superalloy was used to investigate the elementary processes associated with stress-rupture behavior at different temperatures where theγʹrafting occurs.At 900°C,the rupture...A Re-containing Ni-base single crystal superalloy was used to investigate the elementary processes associated with stress-rupture behavior at different temperatures where theγʹrafting occurs.At 900°C,the rupture behavior is mainly determined by the multiplication of dislocations within the wideningγchannels,which is closely linked with the propagation of microcracks along the inherentγ/γʹinterfaces.The rapid formation of lamellaγ/γʹraft structure,along with the developed-well interfacial dislocation networks,and its elastic instability are primarily responsible for the rupture behavior at 1100°C.There is a clear curvature tendency in the Larson-Miller plot of stress-rupture lifetime in relation to stress at high temperatures.It indicates that the influence extent ofγʹrafting on stress-rupture behavior is sensitive to the acting conditions of temperature and stress.展开更多
基金the National Science and Technology Major Project(Nos.J2019-VI-0023-0139 and J2019-VII-0004-0144)the National Natural Science Foundation of China(No.51871221)the National Key R&D Program of China(No.2020YFA0714900).
文摘A Re-containing Ni-base single crystal superalloy was used to investigate the elementary processes associated with stress-rupture behavior at different temperatures where theγʹrafting occurs.At 900°C,the rupture behavior is mainly determined by the multiplication of dislocations within the wideningγchannels,which is closely linked with the propagation of microcracks along the inherentγ/γʹinterfaces.The rapid formation of lamellaγ/γʹraft structure,along with the developed-well interfacial dislocation networks,and its elastic instability are primarily responsible for the rupture behavior at 1100°C.There is a clear curvature tendency in the Larson-Miller plot of stress-rupture lifetime in relation to stress at high temperatures.It indicates that the influence extent ofγʹrafting on stress-rupture behavior is sensitive to the acting conditions of temperature and stress.