Effect of kyanite addition on properties of plastic refractories that based on Chinese calcined flint clay were investigated with the Chinese calcined flint clay as raw materials, aluminum sulfate and fireclay as bind...Effect of kyanite addition on properties of plastic refractories that based on Chinese calcined flint clay were investigated with the Chinese calcined flint clay as raw materials, aluminum sulfate and fireclay as binding systems. After 24 h curing after demoulding and another 24 h curing at 110 ℃, the specimens were heat-treated at 1000, 1300 and 1500℃ for 3 h, respectively. Thepermanent linear change, bulk density, modulus of rupture, clod crushing strength, thermal expansion coefficient and thermal shock resistance were examined. The results show that the shrinkage of plastic refractory decreased with increasing kyanite addition after heat-treated at 1000 and 1300℃ , and its expansivity increased with increasing kyanite addition after heat-treated at 1500 ℃. The strength can be increased when kyanite was added into the plastic refractory. The thermal expansion coefficient and the expansivity were increased, and the shrinkage can be reduced at high temperature when kyanite addition was more than 10%. On the condition of this experiment, the thermal shock resistance of plastic refractory was the best when kyanite addition is w(kyanite)=10%.展开更多
Effect of different particle sizes of cordierite on properties of castable refractory by different heat treatment temperatures were investigated respectively with mullite and bauxite as raw materials, calcium aluminat...Effect of different particle sizes of cordierite on properties of castable refractory by different heat treatment temperatures were investigated respectively with mullite and bauxite as raw materials, calcium aluminate cement as binders. After 24 h curing in mould and another 24 h curing at 110 ℃ after demoulding, the specimens were heat treated at 1 000 ℃, 1 300℃ and 1 500℃ for 3 h, respectively. The bulk density （ BD）, permanent linear change （ PLC）, modulus of rupture（MOR） and clod crushing strength（CCS）, thermal expansion coefficient and thermal shock resistance were examined. The results show that there is no obvious effect on adjusting permanent linear change and bulk density of castables by adding different particle sizes of cordierite at low temperature and intermediate temperature. Modulus of rupture of castable increase with the decreasing of the particle sizes of cordierite after heat treated by 1 000 ℃ and 1 300℃. In this experiment, thermal shock resistance of the castable with cordierite whose particle size is 0 - 1 mm is the best.展开更多
文摘Effect of kyanite addition on properties of plastic refractories that based on Chinese calcined flint clay were investigated with the Chinese calcined flint clay as raw materials, aluminum sulfate and fireclay as binding systems. After 24 h curing after demoulding and another 24 h curing at 110 ℃, the specimens were heat-treated at 1000, 1300 and 1500℃ for 3 h, respectively. Thepermanent linear change, bulk density, modulus of rupture, clod crushing strength, thermal expansion coefficient and thermal shock resistance were examined. The results show that the shrinkage of plastic refractory decreased with increasing kyanite addition after heat-treated at 1000 and 1300℃ , and its expansivity increased with increasing kyanite addition after heat-treated at 1500 ℃. The strength can be increased when kyanite was added into the plastic refractory. The thermal expansion coefficient and the expansivity were increased, and the shrinkage can be reduced at high temperature when kyanite addition was more than 10%. On the condition of this experiment, the thermal shock resistance of plastic refractory was the best when kyanite addition is w(kyanite)=10%.
文摘Effect of different particle sizes of cordierite on properties of castable refractory by different heat treatment temperatures were investigated respectively with mullite and bauxite as raw materials, calcium aluminate cement as binders. After 24 h curing in mould and another 24 h curing at 110 ℃ after demoulding, the specimens were heat treated at 1 000 ℃, 1 300℃ and 1 500℃ for 3 h, respectively. The bulk density （ BD）, permanent linear change （ PLC）, modulus of rupture（MOR） and clod crushing strength（CCS）, thermal expansion coefficient and thermal shock resistance were examined. The results show that there is no obvious effect on adjusting permanent linear change and bulk density of castables by adding different particle sizes of cordierite at low temperature and intermediate temperature. Modulus of rupture of castable increase with the decreasing of the particle sizes of cordierite after heat treated by 1 000 ℃ and 1 300℃. In this experiment, thermal shock resistance of the castable with cordierite whose particle size is 0 - 1 mm is the best.