A three-dimensional coordination polymer,namely {[Zn2（tzba）（dmtrz）（OH）]·3H2O}n（1,H2tzba = 4-（5H-tetrazol）benzoic acid,Hdmtrz = 3,5-dimethyl-lH,l,2,4-triazole）,was hydrothermally synthesized and characte...A three-dimensional coordination polymer,namely {[Zn2（tzba）（dmtrz）（OH）]·3H2O}n（1,H2tzba = 4-（5H-tetrazol）benzoic acid,Hdmtrz = 3,5-dimethyl-lH,l,2,4-triazole）,was hydrothermally synthesized and characterized by single-crystal X-ray diffraction.It crystallizes in monoclinic system,P21/c space group with a = 8.018（11）,b = 21.04（3）,c = 11.069（14） A,β=91.26（3）°,V= 1867（4） A^3,Z = 4,Dc = 1.729 g/cm^3,F（000） = 984,μ= 2.614 mm^（-1）,R（F^2 〉 2σ（F^2）） =0.0612 and wR（F^2） = 0.1533.Topological analysis reveals that compound 1 is a（3,5）-connected structure with a Schlafli symbol of（4~2.6）（4~2.6~5.8~3）,which is a rarely observed lhh topology.In addition,the CO2 adsorption performance and luminescent property of 1 have also been studied.展开更多
A novel compound-monohydrated zinc nicotinate was prepared via room temperature solid phase synthesis and ball grinding.FTIR,chemical and elemental analyses and X-ray powder diffraction technique were applied to chara...A novel compound-monohydrated zinc nicotinate was prepared via room temperature solid phase synthesis and ball grinding.FTIR,chemical and elemental analyses and X-ray powder diffraction technique were applied to characterizing the structure and composition of the complex.Low-temperature heat capacities of the solid coordination compound were measured by a precision automated adiabatic calorimeter over a temperature range from 77 to 400 K.A solid-solid phase transition process occurred in a temperature range of 321―342 K inferred according to the heat capacity curve,and the peak temperature,molar enthalpy and entropy of the phase transition of monohydrated zinc nicotinate were determined to be Ttrs=（340.584±0.829） K,ΔtrsHm=（12.682±0.041） kJ/mol and ΔtrsSm=（37.235±0.101） KJ/mol）.The experimental values of the molar heat capacities in the temperature regions of 77―321 K and 342―400 K were,respectively,fitted to two polynomial equations.In addition,the polynomial fitted values of the molar heat capacities and fundamental thermodynamic functions of the sample relative to the standard reference temperature 298.15 K were calculated and tabulated at intervals of 5 K.展开更多
文摘A three-dimensional coordination polymer,namely {[Zn2（tzba）（dmtrz）（OH）]·3H2O}n（1,H2tzba = 4-（5H-tetrazol）benzoic acid,Hdmtrz = 3,5-dimethyl-lH,l,2,4-triazole）,was hydrothermally synthesized and characterized by single-crystal X-ray diffraction.It crystallizes in monoclinic system,P21/c space group with a = 8.018（11）,b = 21.04（3）,c = 11.069（14） A,β=91.26（3）°,V= 1867（4） A^3,Z = 4,Dc = 1.729 g/cm^3,F（000） = 984,μ= 2.614 mm^（-1）,R（F^2 〉 2σ（F^2）） =0.0612 and wR（F^2） = 0.1533.Topological analysis reveals that compound 1 is a（3,5）-connected structure with a Schlafli symbol of（4~2.6）（4~2.6~5.8~3）,which is a rarely observed lhh topology.In addition,the CO2 adsorption performance and luminescent property of 1 have also been studied.
基金Supported by the National Natural Science Foundation of China(No.20673050)Key Project of Science Foundation from Shaanxi Educational College of China(No.08KJ017)
文摘A novel compound-monohydrated zinc nicotinate was prepared via room temperature solid phase synthesis and ball grinding.FTIR,chemical and elemental analyses and X-ray powder diffraction technique were applied to characterizing the structure and composition of the complex.Low-temperature heat capacities of the solid coordination compound were measured by a precision automated adiabatic calorimeter over a temperature range from 77 to 400 K.A solid-solid phase transition process occurred in a temperature range of 321―342 K inferred according to the heat capacity curve,and the peak temperature,molar enthalpy and entropy of the phase transition of monohydrated zinc nicotinate were determined to be Ttrs=（340.584±0.829） K,ΔtrsHm=（12.682±0.041） kJ/mol and ΔtrsSm=（37.235±0.101） KJ/mol）.The experimental values of the molar heat capacities in the temperature regions of 77―321 K and 342―400 K were,respectively,fitted to two polynomial equations.In addition,the polynomial fitted values of the molar heat capacities and fundamental thermodynamic functions of the sample relative to the standard reference temperature 298.15 K were calculated and tabulated at intervals of 5 K.
