The feasibility of paigeite ore treatment with iron nugget making process is proved. The isothermal reduc- tion experiments at laboratory scale were carried out, using carbon bearing pellets which were made of boron c...The feasibility of paigeite ore treatment with iron nugget making process is proved. The isothermal reduc- tion experiments at laboratory scale were carried out, using carbon bearing pellets which were made of boron contai- ning iron concentrate and pulverized coal mainly, from 1 623 to 1 723 K with different heating time. The results indi- cated that iron nugget making process depends mainly on heating time and temperature. And the iron nugget and slag can separate in a clean manner at 1 673 K for 15 min. For the iron nugget, the C content is 3.57% （mass percent） and B is 0. 065~ （mass percent）. The B203 content of slag is 20.01~/00, and the boron was concentrated into one phase which is identified as suanite （Mg2BaOs） during the solidification. With an extraction ratio of 80~ under the atmospheric conditions, the activity of boron in slag is good. The boron-rich slag can be used to extract boric or boric acid and alleviate the shortage of boron resource. Through series of calculation and analysis related, it can be conclu- ded that the recovery ratio of Fe and boron are about 98% and 97% respectively. The results show that this method is feasible and effective on the utilization of paigeite ore.展开更多
The kinetics of isothermal reduction of the carbon bearing pellets, which were mainly composed of Bayanobo complex iron ore and pulverized coal, was investigated by thermogravimetry at the temperature of 1 273-1 673 K...The kinetics of isothermal reduction of the carbon bearing pellets, which were mainly composed of Bayanobo complex iron ore and pulverized coal, was investigated by thermogravimetry at the temperature of 1 273-1 673 K. The effects of xC/xO and the atmospheres on the extent of reduction also were investigated. The results indicate that the fractional reaction increased proportionally with temperature increasing and heating temperature is the significant influence factor to the reaction of carbon bearing pellets. The optimum xC/xO is 1.2 and the effect of atmosphere on the reduction of iron oxides is almost negligible. The results can be interpreted that the reaction was initially controlled by a mixed controlled mechanism of carbon gasification and interface chemical reaction, and in the later stage, interface chemical reaction became the rate-controlling step. Apparent activation energy values of reduction at different levels of fractional reaction were calculated. Before F （fraction of reaction）=0.5, the apparent activation energy ranges from 66.39 to 75.64 kJ/mol, while after F=0.5, the apparent activation energy is 80.98 to 85.37 kJ/mol.展开更多
基金Sponsored by National Key Technology Research and Development Program in 11th Five-Year Plan of China (2008BAB32B05)
文摘The feasibility of paigeite ore treatment with iron nugget making process is proved. The isothermal reduc- tion experiments at laboratory scale were carried out, using carbon bearing pellets which were made of boron contai- ning iron concentrate and pulverized coal mainly, from 1 623 to 1 723 K with different heating time. The results indi- cated that iron nugget making process depends mainly on heating time and temperature. And the iron nugget and slag can separate in a clean manner at 1 673 K for 15 min. For the iron nugget, the C content is 3.57% （mass percent） and B is 0. 065~ （mass percent）. The B203 content of slag is 20.01~/00, and the boron was concentrated into one phase which is identified as suanite （Mg2BaOs） during the solidification. With an extraction ratio of 80~ under the atmospheric conditions, the activity of boron in slag is good. The boron-rich slag can be used to extract boric or boric acid and alleviate the shortage of boron resource. Through series of calculation and analysis related, it can be conclu- ded that the recovery ratio of Fe and boron are about 98% and 97% respectively. The results show that this method is feasible and effective on the utilization of paigeite ore.
基金Sponsored by National Key Technology Research and Development Program of China(2008BAB32B05)Postdoctoral Science Foundation of China(2012m510320)
文摘The kinetics of isothermal reduction of the carbon bearing pellets, which were mainly composed of Bayanobo complex iron ore and pulverized coal, was investigated by thermogravimetry at the temperature of 1 273-1 673 K. The effects of xC/xO and the atmospheres on the extent of reduction also were investigated. The results indicate that the fractional reaction increased proportionally with temperature increasing and heating temperature is the significant influence factor to the reaction of carbon bearing pellets. The optimum xC/xO is 1.2 and the effect of atmosphere on the reduction of iron oxides is almost negligible. The results can be interpreted that the reaction was initially controlled by a mixed controlled mechanism of carbon gasification and interface chemical reaction, and in the later stage, interface chemical reaction became the rate-controlling step. Apparent activation energy values of reduction at different levels of fractional reaction were calculated. Before F （fraction of reaction）=0.5, the apparent activation energy ranges from 66.39 to 75.64 kJ/mol, while after F=0.5, the apparent activation energy is 80.98 to 85.37 kJ/mol.