The modified petroleum resin emulsion prepared from the C9petroleum resin was modified with maleic anhydride.The effects of maleic rosin and maleic anhydride addition level,the modification time and the alkali liquor ...The modified petroleum resin emulsion prepared from the C9petroleum resin was modified with maleic anhydride.The effects of maleic rosin and maleic anhydride addition level,the modification time and the alkali liquor on the properties of the emulsion were discussed.The results showed that the optimum process conditions covered:a maleic anhydride mass fraction of 1.5%,a maleic rosin mass fraction of 10%,a KOH mass fraction of 1%,a petroleum resin modification temperature of 200℃,a petroleum resin modification duration of 3 h,and a modified petroleum resin emulsion/wax emulsion mixing ratio of 1:1.The particle size of modified petroleum resin emulsion prepared under these conditions was equal to 104.166μm.展开更多
A silicone oil emulsion with 60% of solid content was prepared with methyl silicone oil used as the main material by means of the emulsifier-in-oil method.The influence of emulsification conditions on the droplet diam...A silicone oil emulsion with 60% of solid content was prepared with methyl silicone oil used as the main material by means of the emulsifier-in-oil method.The influence of emulsification conditions on the droplet diameter of silicone oil emulsion was discussed.The experimental results showed that the emulsification method,including the quantity of the emulsifier,the time and temperature of emulsification,the emulsifying water dosage,and the stirring speed,had significant impact on the droplet size.The optimal conditions were identified to achieve a smallest droplet diameter of the emulsion at an emulsifier dosage of 6%,an emulsification temperature of 70 ℃,an emulsification time of 30 min,and a stirring speed of 1100 r/min,with water added in two portions at a ratio of 1:1.The high-solid content silicone oil emulsion with a mean droplet diameter of 2.731 μm was prepared under these conditions that could ensure absence of stratification and floating oil under centrifuging at a speed of 3000 r/min for 30 min.展开更多
The paraffin wax microemulsion was prepared from fully refined paraffin wax No.58-60 in the presence of a nonionic surfactant and an anionic surfactant.The influence of manufacturing parameters on the particle diamete...The paraffin wax microemulsion was prepared from fully refined paraffin wax No.58-60 in the presence of a nonionic surfactant and an anionic surfactant.The influence of manufacturing parameters on the particle diameter of paraffin wax microemulsion included the quantity of the emulsifier,the temperature and emulsification time,the stirring speed,the pH value and the auxiliary ingredient(cosurfactant).The test results showed that the temperature of emulsification had little effect on the particle size of paraffin wax microemulsion in a temperature range of 75-85 ℃.Other manufacturing parameters all had a great effect on the particle size of paraffin wax microemulsion.The optimum preparation conditions included:a w(emulsifier) of 6%,an emulsification temperature of 80 ℃,an emulsification time of 40 min,a pH value of about 8,and a stirring speed of 600 r/min,with n-amyl alcohol serving as the co-surfactant.Under these conditions,a translucent and baby blue paraffin wax emulsion was prepared with its particle size equating to 97 nm.展开更多
文摘The modified petroleum resin emulsion prepared from the C9petroleum resin was modified with maleic anhydride.The effects of maleic rosin and maleic anhydride addition level,the modification time and the alkali liquor on the properties of the emulsion were discussed.The results showed that the optimum process conditions covered:a maleic anhydride mass fraction of 1.5%,a maleic rosin mass fraction of 10%,a KOH mass fraction of 1%,a petroleum resin modification temperature of 200℃,a petroleum resin modification duration of 3 h,and a modified petroleum resin emulsion/wax emulsion mixing ratio of 1:1.The particle size of modified petroleum resin emulsion prepared under these conditions was equal to 104.166μm.
文摘A silicone oil emulsion with 60% of solid content was prepared with methyl silicone oil used as the main material by means of the emulsifier-in-oil method.The influence of emulsification conditions on the droplet diameter of silicone oil emulsion was discussed.The experimental results showed that the emulsification method,including the quantity of the emulsifier,the time and temperature of emulsification,the emulsifying water dosage,and the stirring speed,had significant impact on the droplet size.The optimal conditions were identified to achieve a smallest droplet diameter of the emulsion at an emulsifier dosage of 6%,an emulsification temperature of 70 ℃,an emulsification time of 30 min,and a stirring speed of 1100 r/min,with water added in two portions at a ratio of 1:1.The high-solid content silicone oil emulsion with a mean droplet diameter of 2.731 μm was prepared under these conditions that could ensure absence of stratification and floating oil under centrifuging at a speed of 3000 r/min for 30 min.
基金supported by The National Natural Science Funds (Project No. 21076025)
文摘The paraffin wax microemulsion was prepared from fully refined paraffin wax No.58-60 in the presence of a nonionic surfactant and an anionic surfactant.The influence of manufacturing parameters on the particle diameter of paraffin wax microemulsion included the quantity of the emulsifier,the temperature and emulsification time,the stirring speed,the pH value and the auxiliary ingredient(cosurfactant).The test results showed that the temperature of emulsification had little effect on the particle size of paraffin wax microemulsion in a temperature range of 75-85 ℃.Other manufacturing parameters all had a great effect on the particle size of paraffin wax microemulsion.The optimum preparation conditions included:a w(emulsifier) of 6%,an emulsification temperature of 80 ℃,an emulsification time of 40 min,a pH value of about 8,and a stirring speed of 600 r/min,with n-amyl alcohol serving as the co-surfactant.Under these conditions,a translucent and baby blue paraffin wax emulsion was prepared with its particle size equating to 97 nm.