A novel melting infiltration by ultrasonic vibration was investigated and applied to fabricate Ti6Al4V(TC4)lattice structure-reinforced Mg-10Gd-2Y-1Zn-xZr(refer to VW92 hereafter,x=0,0.5 wt%)alloy matrix composites.Th...A novel melting infiltration by ultrasonic vibration was investigated and applied to fabricate Ti6Al4V(TC4)lattice structure-reinforced Mg-10Gd-2Y-1Zn-xZr(refer to VW92 hereafter,x=0,0.5 wt%)alloy matrix composites.The edge-to-edge matching model indicates that the well-matching and possible orientation relationships(ORs)between theα-Mg andα-Ti,[10-10]_(α-Mg)//[11-23]_(α-Ti) in(0002)_(α-Mg)//(10-10)_(α-Ti) possesses the smallest misfit of 0.4%(f_(r)),and thus theα-Mg grains can nucleate on the TC4 lattice structure.Interfacial reaction occurred in the TC4/VW92+0.5 wt%Zr composites,and the reaction product was confirmed to be Al_(2)Zr_(3),AlZr_(2) andα-Ti(Zr)particles formed by continuous solution of Zr-Ti.Among the interfacial products,the AlZr_(2) phase is a brittle phase with high-volume fraction,which is not conducive to the load transfer.But generally speaking,theα-Ti(Zr)and theα-Mg tend to form a coherent interface,which is beneficial for improving the interfacial bonding strength of composites.展开更多
基金supported by the Guangdong Major Project of Basic and Applied Basic Research (2020B0301030006)the National Natural Science Foundation of China (52225101)+2 种基金the Scientific Research Foundation of Chongqing University of Technology (2020ZDZ006)the Science and Technology Research Program of the Chongqing Municipal Education Commission (KJZD-K202201108)the University Innovation Research Group of Chongqing (CXQT20023).
文摘A novel melting infiltration by ultrasonic vibration was investigated and applied to fabricate Ti6Al4V(TC4)lattice structure-reinforced Mg-10Gd-2Y-1Zn-xZr(refer to VW92 hereafter,x=0,0.5 wt%)alloy matrix composites.The edge-to-edge matching model indicates that the well-matching and possible orientation relationships(ORs)between theα-Mg andα-Ti,[10-10]_(α-Mg)//[11-23]_(α-Ti) in(0002)_(α-Mg)//(10-10)_(α-Ti) possesses the smallest misfit of 0.4%(f_(r)),and thus theα-Mg grains can nucleate on the TC4 lattice structure.Interfacial reaction occurred in the TC4/VW92+0.5 wt%Zr composites,and the reaction product was confirmed to be Al_(2)Zr_(3),AlZr_(2) andα-Ti(Zr)particles formed by continuous solution of Zr-Ti.Among the interfacial products,the AlZr_(2) phase is a brittle phase with high-volume fraction,which is not conducive to the load transfer.But generally speaking,theα-Ti(Zr)and theα-Mg tend to form a coherent interface,which is beneficial for improving the interfacial bonding strength of composites.