Core-shell structured cobalt coated tungsten carbide（WC/Co） composite powders were prepared by intermittent electrodeposition. The influence of process parameters such as current density, single deposition pulse, p ...Core-shell structured cobalt coated tungsten carbide（WC/Co） composite powders were prepared by intermittent electrodeposition. The influence of process parameters such as current density, single deposition pulse, p H value and surfactants on the formation of WC/Co was investigated and characterized by scanning electron microscopy（SEM）, electrochemical station, acidometer and X-ray diffraction（XRD） techniques.The composite powders with 54% cobalt content were fabricated at a current density of 16 A dm-2, with a load of 10 g dm-3WC powders and a stirring speed of 600 r min-1at an operation temperature of 40 ± 2 °C,and 90% current efficiency was obtained with a single deposition pulse of 1.5 min and single stirring pulse of 2 min during 12 min efficient electrodeposition time. The uniformly distributed WC/Co powders could be obtained in the cobalt electrolyte containing 300 mg dm-3PEG-2000. The spherical cobalt grains coated WC particles were prepared in the p H 4-5 electrolyte at the Co deposition rate of 0.58 g min-1. A practical process for high efficient production of WC/Co powders by electrodeposition was developed in the present work.展开更多
基金jointly funded by the National Natural Science Foundation of China(Nos.21476066 and 51271074)the Key Project of Hunan provincial Education Department of China(No.15A146)
文摘Core-shell structured cobalt coated tungsten carbide（WC/Co） composite powders were prepared by intermittent electrodeposition. The influence of process parameters such as current density, single deposition pulse, p H value and surfactants on the formation of WC/Co was investigated and characterized by scanning electron microscopy（SEM）, electrochemical station, acidometer and X-ray diffraction（XRD） techniques.The composite powders with 54% cobalt content were fabricated at a current density of 16 A dm-2, with a load of 10 g dm-3WC powders and a stirring speed of 600 r min-1at an operation temperature of 40 ± 2 °C,and 90% current efficiency was obtained with a single deposition pulse of 1.5 min and single stirring pulse of 2 min during 12 min efficient electrodeposition time. The uniformly distributed WC/Co powders could be obtained in the cobalt electrolyte containing 300 mg dm-3PEG-2000. The spherical cobalt grains coated WC particles were prepared in the p H 4-5 electrolyte at the Co deposition rate of 0.58 g min-1. A practical process for high efficient production of WC/Co powders by electrodeposition was developed in the present work.