Effect of heat treatment on microstructural evolution,mechanical properties and tribological properties of H13 steel prepared using selective laser melting

H13 tool steel was successfully prepared by selective laser melting(SLM)technology.The effects of heat treatment on the microstructure,mechanical properties,and tribological properties of SLMed H13 steel were investigated.The heat treatment process involved a solution treatment and a double aging treatment of the deposited H13 tool steel prepared by SLM.The aim is to optimize the microstructure and mechanical properties of SLMed H13 steel.Due to the rapid heating and cooling effects of SLM,carbide precipitation in the deposited H13 steel was not uniform and residual stresses were present.The purpose of the solution treatment is to dissolve the solution at a high temperature to eliminate the residual stresses and defects introduced by the SLM-forming structure.The solution treatment and first aging treatment produced the precipitation of small carbides at the grain boundaries and inside the crystals,which increased the hardness of SLMed H13 steel.The hardness increased from 538±4.0 HV of the as-deposited sample to 548±5.8 HV of samples after the first aging treatment.Accordingly,the ultimate tensile strength and the elongation at break decreased from 1882 MPa and 11.5%in the as-deposited sample to 1697 MPa and 7.9%in those after the first aging treatment,respectively.Furthermore,the friction coefficient and wear rate in the as-deposited sample decreased from 0.5160 and 2.36×10^(–6)mm^(−3)N^(−1)m^(−1)to 0.4244 and 1.04×10^(–6)mm^(−3)N^(−1)m^(−1),respectively.However,the distribution of carbides inside the crystals was not uniform.The second aging treatment adjusted the morphology of carbide precipitation and made it more uniform,but the precipitation of carbides grew and settled at the bottom of the grain boundaries.The hardness decreased to 533±6.7 HV compared with that with the first aging treatment,but the ultimate tensile strength and plasticity reached a balance(1807 MPa,14.05%).Accordingly,the friction coefficient and wear rate also showed a stable and decreasing trend(0.4407,0.98×10^(–6)mm^(−3)N^(−1)m^(−1)).

Phase Transformation of a Cold Work Tool Steel during Tempering

The hardness and microstructure evolution of a 8% Cr cold work tool steel during tempering for 40 h were investigated. Transmission electron microscope examinations showed that M_3C carbides precipitated from supersaturated martensite after tempering at 350 ℃. When the tempering temperature was higher than 520 ℃,the M_（23）C_6 carbides precipitated to substitute for M_3C carbides. After ageing at the temperature of 520 ℃ for 40 h,it was observed that very fine and dense secondary Mo_2C precipitates were precipitated. Thus,it can be concluded that the early stage of Mo_2C-carbide precipitation is like to be Gunier-Preston（ G-P） zone formed by [Mo-C] segregation group which is responsible for the secondary hardening peak at 520 ℃. Overageing at 700 ℃ resulted in recovery of martensitic microstructure and precipitation of M_（23）C_6 carbides.When ageing at 700 ℃ for more than 20 h,recrystallization occurred,which resulted in a change of the matrix morphology from martensitic plates to equiaxed ferrite. It was noticed that the size of recrystallized grain / subgrain was very fine,which was attributed to the pinning effect of M_（23）C_6 precipitates.