To protect the AM60B magnesium alloy from corrosion,a sol-gel coating containing hydroxylated g-C_(3)N_(4)nanoplates was applied.The chemical composition of the hydroxylated g-C_(3)N_(4)nanoplates was investigated usi...To protect the AM60B magnesium alloy from corrosion,a sol-gel coating containing hydroxylated g-C_(3)N_(4)nanoplates was applied.The chemical composition of the hydroxylated g-C_(3)N_(4)nanoplates was investigated using X-ray photoelectron spectroscopy(XPS).The hydroxylation process did not affect the crystal size,specific surface area,pore volume,average pore diameter,and thermal stability of the g-C_(3)N_(4)nanoplates.After incorporating pristine and hydroxylated g-C_(3)N_(4)nanoplates,dense sol-gel coatings were obtained.Transmission electron microscopy(TEM)revealed the uniform distribution of the modified g-C_(3)N_(4)in the coating.The average roughness of the coating was also reduced after adding the modified nanoplates due to the decreased aggregation tendency.Electrochemical impedance spectroscopy(EIS)examinations in simulated acid rain revealed a significant improvement in the anticorrosion properties of the sol-gel film after the addition of the modified g-C_(3)N_(4)due to the chemical bonding of the coating to the nanoplates.展开更多
8-hydroxyquinoline(8-HQ)intercalated layered double hydroxides(LDH)film as underlayer and sol-gel layer was combined for active corrosion protection of the AM60B magnesium alloy.The LDH,LDH/sol-gel,and LDH@HQ/sol-gel ...8-hydroxyquinoline(8-HQ)intercalated layered double hydroxides(LDH)film as underlayer and sol-gel layer was combined for active corrosion protection of the AM60B magnesium alloy.The LDH,LDH/sol-gel,and LDH@HQ/sol-gel coatings were analyzed using the scanning electron microscopy(SEM),field emission scanning electron microscopy(FESEM),energy dispersive X-ray spectroscopy(EDS),X-ray diffraction(XRD),atomic force microscopy(AFM),and electrochemical impedance spectroscopy(EIS)methods.The SEM images showed that the surface was entirely coated by the LDH film composed of vertically-grown nanosheets.The same morphology was observed for the LDH/sol-gel and LDH@HQ/sol-gel coatings.Also,almost the same topography was observed for both composite coatings except that the LDH@HQ/sol-gel coating had relatively higher surface roughness.Although the LDH film had the same impedance behavior as the alloy sample in 3.5wt%NaCl solution,its corrosion resistance was much higher,which could be due to its barrier properties as well as to the trap-ping of the chloride ions.Similar to the LDH film,the corrosion resistance of the LDH/sol-gel composite diminished with increasing the ex-posure time.However,its values were much higher than that of the LDH film,which was mainly related to the sealing of the solution path-ways.The LDH@HQ/sol-gel composite showed much better anti-corrosion properties than the LDH/sol-gel coating due to the adsorption of the 8-HQ on the damaged areas through the complexation.展开更多
The g-C3 N4/Fe3 O4/MnWO4 nanocomposites were prepared by a refluxing-calcination procedure. Visiblelight-induced photocatalytic experiments showed that the g-C3 N4/Fe3 O4/MnWO4(10%) nanocomposite has excellent abili...The g-C3 N4/Fe3 O4/MnWO4 nanocomposites were prepared by a refluxing-calcination procedure. Visiblelight-induced photocatalytic experiments showed that the g-C3 N4/Fe3 O4/MnWO4(10%) nanocomposite has excellent ability to degrade a range of contaminants including rhodamine B, methylene blue, methyl orange, and fuchsine, which is about 7, 10, 25, and 31 times of the g-C3 N4 photocatalyst, respectively.Reactive species trapping experiments revealed that superoxide anion radicals play major role in the photodegradation reaction of rhodamine B(RhB). After the treatment process, the utilized photocatalyst was magnetically recovered and reused with negligible loss in the photocatalytic activity, which is vital in the photocatalytic processes. Finally, a mechanism was proposed for the enhanced interfacial carrier separation and transfer and the improved photocatalytic performance.展开更多
文摘To protect the AM60B magnesium alloy from corrosion,a sol-gel coating containing hydroxylated g-C_(3)N_(4)nanoplates was applied.The chemical composition of the hydroxylated g-C_(3)N_(4)nanoplates was investigated using X-ray photoelectron spectroscopy(XPS).The hydroxylation process did not affect the crystal size,specific surface area,pore volume,average pore diameter,and thermal stability of the g-C_(3)N_(4)nanoplates.After incorporating pristine and hydroxylated g-C_(3)N_(4)nanoplates,dense sol-gel coatings were obtained.Transmission electron microscopy(TEM)revealed the uniform distribution of the modified g-C_(3)N_(4)in the coating.The average roughness of the coating was also reduced after adding the modified nanoplates due to the decreased aggregation tendency.Electrochemical impedance spectroscopy(EIS)examinations in simulated acid rain revealed a significant improvement in the anticorrosion properties of the sol-gel film after the addition of the modified g-C_(3)N_(4)due to the chemical bonding of the coating to the nanoplates.
文摘8-hydroxyquinoline(8-HQ)intercalated layered double hydroxides(LDH)film as underlayer and sol-gel layer was combined for active corrosion protection of the AM60B magnesium alloy.The LDH,LDH/sol-gel,and LDH@HQ/sol-gel coatings were analyzed using the scanning electron microscopy(SEM),field emission scanning electron microscopy(FESEM),energy dispersive X-ray spectroscopy(EDS),X-ray diffraction(XRD),atomic force microscopy(AFM),and electrochemical impedance spectroscopy(EIS)methods.The SEM images showed that the surface was entirely coated by the LDH film composed of vertically-grown nanosheets.The same morphology was observed for the LDH/sol-gel and LDH@HQ/sol-gel coatings.Also,almost the same topography was observed for both composite coatings except that the LDH@HQ/sol-gel coating had relatively higher surface roughness.Although the LDH film had the same impedance behavior as the alloy sample in 3.5wt%NaCl solution,its corrosion resistance was much higher,which could be due to its barrier properties as well as to the trap-ping of the chloride ions.Similar to the LDH film,the corrosion resistance of the LDH/sol-gel composite diminished with increasing the ex-posure time.However,its values were much higher than that of the LDH film,which was mainly related to the sealing of the solution path-ways.The LDH@HQ/sol-gel composite showed much better anti-corrosion properties than the LDH/sol-gel coating due to the adsorption of the 8-HQ on the damaged areas through the complexation.
基金the financial support from University of Mohaghegh Ardabili
文摘The g-C3 N4/Fe3 O4/MnWO4 nanocomposites were prepared by a refluxing-calcination procedure. Visiblelight-induced photocatalytic experiments showed that the g-C3 N4/Fe3 O4/MnWO4(10%) nanocomposite has excellent ability to degrade a range of contaminants including rhodamine B, methylene blue, methyl orange, and fuchsine, which is about 7, 10, 25, and 31 times of the g-C3 N4 photocatalyst, respectively.Reactive species trapping experiments revealed that superoxide anion radicals play major role in the photodegradation reaction of rhodamine B(RhB). After the treatment process, the utilized photocatalyst was magnetically recovered and reused with negligible loss in the photocatalytic activity, which is vital in the photocatalytic processes. Finally, a mechanism was proposed for the enhanced interfacial carrier separation and transfer and the improved photocatalytic performance.