Microstructures and mechanical properties of SiBCNAl ceramics produced by mechanical alloying and subsequent hot pressing

Amorphous SiBCNAl powders were prepared via a mechanical alloying (MA) technique using crystalline silicon (Si), hexagonal boron nitride (h-BN), graphite (C), and aluminum (Al) as starting materials. SiBCNAl powders were consolidated by a hot pressing (HP) technique at 1800 °C under a pressure of 30 MPa in argon and nitrogen. The sintering atmosphere had a great influence on the microstructures and mechanical properties of the ceramics. The two ceramics had different phase compositions and fracture surface morphologies. For the ceramics sintered in argon, flexural strength, fracture toughness, elastic modulus and Vickers hardness were 421.90 MPa, 3.40 MPa·m1/2, 174.10 GPa, and 12.74 GPa, respectively. For the ceramics sintered in nitrogen, the mechanical properties increased, except for the Vickers hardness, and the values of the above properties were 526.80 MPa, 5.25 MPa·m1/2, 222.10 GPa, and 11.63 GPa, respectively.

Microstructural evolution and mechanical properties of h-BN composite ceramics with Y2O3-AlN addition by liquid-phase sintering

Hexagonal boron nitride(h-BN)composite ceramics were prepared by hot pressing with the addition of Y2O3 and AlN.The effects of different Y2O3–AlN contents on microstructural evolution,mechanical properties and thermal diffusion coefficients of h-BN composite ceramics were investigated.The results indicate that Y2O3–AlN forms a liquid phase during the sintering process achieving a good wettability with h-BN grains.In pure h-BN ceramic and h-BN composite ceramic with 40 wt%Y2O3–AlN,the h-BN grains grow well when controlled through solid-phase and liquid-phase diffusion,respectively.With the increase in Y2O3–AlN content,mechanical properties and thermal diffusion coefficients of h-BN composite ceramics first decrease and then increase,and the properties of h-BN composite ceramic with 10 wt%Y2O3–AlN are the inflection points.Such properties are highly related to the phase compositions,porosity and microstructure.

Biocorrosion resistance of coated magnesium alloy by microarc oxidation in electrolyte containing zirconium and calcium salts

The key to use magnesium alloys as suitable biodegradable implants is how to adjust their degradation rates. We report a strategy to prepare biocompatible ceramic coating with improved biocorrosion resistance property on AZ91D alloy by microarc oxidation （MAO） in a silicate-K2ZrF6 solution with and without Ca（H2PO4）2 additives. The microstructure and biocorrosion of coatings were characterized by XRD and SEM, as well as electrochemical and immersion tests in simulated body fluid （SBF）. The results show that the coatings are mainly composed of MgO, Mg2SiO4, m-ZrO2 phases, further Ca containing compounds involve the coating by Ca（H2PO4）2 addition in the silicate-K2ZrF6 solution. The corrosion resistance of coated AZ91D alloy is significantly improved compared with the bare one. After immersing in SBF for 28 d, the Si-Zr5-CaO coating indicates a best corrosion resistance performance.

Printing and electromagnetic characteristics of 3D printing frequency selective surface using graphene

The study of Frequency Selective Surface(FSS)by Direct ink writing(DIW)has attracted much attention due to the convenience and effectiveness of 3D printing technology.However,the limited printing precision of DIW has heavily restricted its applications as the electromagnetic performance is highly sensitive to it,especially the precision at the microscale.Herein,the ultra-high printing precision of FSS was achieved through DIW by the uniformly dispersed graphene sheets to deeply modify the rheological behavior and the steric hindrance effect.Thus,the highly precision of the printed filament width as thin as67μm with a space of only 42μm were achieved,which is difficult for conventional DIW,and no structural distortion is found after 3D printing,no matter it was 2D printed on a flat surface or the sharply skewed hook face,or even 3D printed to architectural structures.According to the highly improved precision,the electromagnetic performance matching between the designed model and the printed physical FSS device was perfectly achieved,reducing the center frequency error less than 0.3 GHz,and the transmission coefficient error less than 0.046.Our work promises an effective and easy preparation of high-quality FSS from the aid of graphene.