The solidifi cation structures of alloy 800 H fabricated with and without linear electromagnetic stirring(L-EMS) were investigated. The results show that the solidification structure of the alloy can be obviously affe...The solidifi cation structures of alloy 800 H fabricated with and without linear electromagnetic stirring(L-EMS) were investigated. The results show that the solidification structure of the alloy can be obviously affected by the forced convection in melt caused by L-EMS. The average size of equiaxed grains of the alloy with L-EMS decreases from 3.5 mm to 2.3 mm, and the ratio of equiaxed grain increases from 5% to 43% compared with that without L-EMS. The microstructure of the alloy without L-EMS is composed of f ine equiaxed dendrites in the outermost layer and columnar dendrites in other areas, whereas that with L-EMS contains equiaxed dendrites, columnar dendrites and cross dendrites. In addition, the mechanism of dendrite fragment drift was proved by examining the composition change of the main alloying elements in the dendrite trunks at different solidifi cation stage using an electron probe micro-analyzer(EPMA).展开更多
基金financially supported by the National Nature Science Foundation of China(No.50834009)the Key(Key Grant)Project of the Ministry of Education of P.R.China(No.311014)+1 种基金the Fundamental Research Funds for the Central Universities of China(No.N090609001 and No.N100409005)the Programme of Introducing Talents of Discipline to Universities(the 111 Project of China,No.B07015)
文摘The solidifi cation structures of alloy 800 H fabricated with and without linear electromagnetic stirring(L-EMS) were investigated. The results show that the solidification structure of the alloy can be obviously affected by the forced convection in melt caused by L-EMS. The average size of equiaxed grains of the alloy with L-EMS decreases from 3.5 mm to 2.3 mm, and the ratio of equiaxed grain increases from 5% to 43% compared with that without L-EMS. The microstructure of the alloy without L-EMS is composed of f ine equiaxed dendrites in the outermost layer and columnar dendrites in other areas, whereas that with L-EMS contains equiaxed dendrites, columnar dendrites and cross dendrites. In addition, the mechanism of dendrite fragment drift was proved by examining the composition change of the main alloying elements in the dendrite trunks at different solidifi cation stage using an electron probe micro-analyzer(EPMA).