In order to improve the tensile property, flexuralproperty and drying shrinkage of strain-hardening cementitiouscomposites （SHCC）, mixtures quantitatively modified withsuperabsorbent polymer （SAP） were investigate...In order to improve the tensile property, flexuralproperty and drying shrinkage of strain-hardening cementitiouscomposites （SHCC）, mixtures quantitatively modified withsuperabsorbent polymer （SAP） were investigated. Theuniaxial tensile test, the four-point bending test, thecompressive test, the drying shrinkage test and theenvironmental scanning electron microscope （ESEM） wereemployed to investigate the tensile strain capacity, flexuraldeformation capacity, compressive strength, drying shrinkage,crack width and self-healing of SHCC. The experimentalresults show that SHCC modified with SAP particles exhibitsexcellent ductility and deformability, and the tensile strain isup to about 4.5% and the average crack width is controlledaround 40 μm. Meanwhile, the drying shrinkage of SHCCmodified with SAP particles can reduce by about 60%.Furthermore, the self-healing behavior is observed in thecracks of specimen after three cycles of high-low relativehumidity curing, and the self-healing products can completelyfill the cracks of SHCC specimens modified with SAPparticles. It is, therefore, feasible to produce SHCC materialmodified with SAP particles, while simultaneously retaininghigher material ductility.展开更多
基金The National Natural Science Foundation of China(No.51278097)Start-up Grant provided by Nanyang Technological University(No.M4081208)
文摘In order to improve the tensile property, flexuralproperty and drying shrinkage of strain-hardening cementitiouscomposites （SHCC）, mixtures quantitatively modified withsuperabsorbent polymer （SAP） were investigated. Theuniaxial tensile test, the four-point bending test, thecompressive test, the drying shrinkage test and theenvironmental scanning electron microscope （ESEM） wereemployed to investigate the tensile strain capacity, flexuraldeformation capacity, compressive strength, drying shrinkage,crack width and self-healing of SHCC. The experimentalresults show that SHCC modified with SAP particles exhibitsexcellent ductility and deformability, and the tensile strain isup to about 4.5% and the average crack width is controlledaround 40 μm. Meanwhile, the drying shrinkage of SHCCmodified with SAP particles can reduce by about 60%.Furthermore, the self-healing behavior is observed in thecracks of specimen after three cycles of high-low relativehumidity curing, and the self-healing products can completelyfill the cracks of SHCC specimens modified with SAPparticles. It is, therefore, feasible to produce SHCC materialmodified with SAP particles, while simultaneously retaininghigher material ductility.