The effects of quenching temperature, cooling pattern, temper temperature andtemper times on the structure and properti-es of high speed steel (HSS) rolls have beeninvestigated. The results show that, when the quenchi...The effects of quenching temperature, cooling pattern, temper temperature andtemper times on the structure and properti-es of high speed steel (HSS) rolls have beeninvestigated. The results show that, when the quenching temperature is lower than 1050℃ thehardness of HSS increases with the quenching temperature increasing in oil cooling, but when thequenching temperature exceeds 1100℃ the hardness decreases. In the conditions of salt bath coolingand air cooling, the effect of quenching temperature on the hardness is similar to the above law,but the quenching temperature obtaining the highest hardness is higher than that in oil cooling.When the temper temperature below 350℃ the hardness of HSS has a little change, when above 475℃the hardness will increase with the temper temperature increasing, and the highest hardness isobtained at 525℃. When the temper temperature continues to increase, the hardness decreases. Twicetemper has little effect on the hardness, but three times temper decreases the hardness. HSS in aircooling has lower hardenability, oil cooling can easily produce crackle, and HSS quenching in saltbath has high harde-nability and excellent wear resistance.展开更多
文摘The effects of quenching temperature, cooling pattern, temper temperature andtemper times on the structure and properti-es of high speed steel (HSS) rolls have beeninvestigated. The results show that, when the quenching temperature is lower than 1050℃ thehardness of HSS increases with the quenching temperature increasing in oil cooling, but when thequenching temperature exceeds 1100℃ the hardness decreases. In the conditions of salt bath coolingand air cooling, the effect of quenching temperature on the hardness is similar to the above law,but the quenching temperature obtaining the highest hardness is higher than that in oil cooling.When the temper temperature below 350℃ the hardness of HSS has a little change, when above 475℃the hardness will increase with the temper temperature increasing, and the highest hardness isobtained at 525℃. When the temper temperature continues to increase, the hardness decreases. Twicetemper has little effect on the hardness, but three times temper decreases the hardness. HSS in aircooling has lower hardenability, oil cooling can easily produce crackle, and HSS quenching in saltbath has high harde-nability and excellent wear resistance.