The effects of different aging processes on the microstructure and mechanical properties of a novel Al-Cu-Li alloy have been investigated by X-ray diffraction, scanning electron microscopy and transmission electron mi...The effects of different aging processes on the microstructure and mechanical properties of a novel Al-Cu-Li alloy have been investigated by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. It is found that the tensile properties of a novel Al-Cu-Li alloy are sensitive to aging processes, which correspond to different microstructures. σ（Al_5Cu_6Mg_2） and T_1（Al_2CuLi） phases are the major precipitates for the alloy in T6 aging condition（165 ℃/60 h）. After duplex aging condition（150 ℃/24 h ＋ 180 ℃/12 h）, σ, θ＇（Al_2Cu） and T_1 phases are detected. Only the T_1 phases can be found in the T8 state alloy（6% pre-strain＋135 ℃/60 h）. The failure modes of alloy in T6 and duplex aging conditions are dimple-intergranular fracture, while typical quasi-cleavage fracture in T8 condition.展开更多
本文利用一种新的聚苯乙烯(PS)微乳液的凝胶化现象,制备了结构稳定的PS凝胶,并通过可控的毛细收缩过程获得了具有不同孔隙结构的PS块体.对PS微乳液的凝胶化机制的系统研究表明,在PS微乳液中加入适量特定的水溶性有机溶剂后,可实现PS微...本文利用一种新的聚苯乙烯(PS)微乳液的凝胶化现象,制备了结构稳定的PS凝胶,并通过可控的毛细收缩过程获得了具有不同孔隙结构的PS块体.对PS微乳液的凝胶化机制的系统研究表明,在PS微乳液中加入适量特定的水溶性有机溶剂后,可实现PS微乳液的破乳,PS乳胶粒子周围的表面活性剂完全解吸附,并自发团聚成二次颗粒,在适当温度条件下可通过分子链缠结组装形成三维多孔凝胶.不同溶剂实现PS微乳液凝胶化的能力可以通过d2T/η参数的大小衡量和评估.通过进一步调整成胶时间与溶剂置换程度,PS凝胶可在后续的干燥过程中实现不同程度的收缩,从而得到密度范围在0.06–1.14 g cm^(-3)的多孔或致密PS块体.这种PS凝胶化策略是一种简单高效的PS成型方法,避免了成型设备、模板、成孔剂以及大量表面活性剂的应用,有望成为制备功能高分子聚合物块体材料的新方法.展开更多
基金the National High Technology Research and Development Program of China (Grant No.2013AA032401)
文摘The effects of different aging processes on the microstructure and mechanical properties of a novel Al-Cu-Li alloy have been investigated by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. It is found that the tensile properties of a novel Al-Cu-Li alloy are sensitive to aging processes, which correspond to different microstructures. σ（Al_5Cu_6Mg_2） and T_1（Al_2CuLi） phases are the major precipitates for the alloy in T6 aging condition（165 ℃/60 h）. After duplex aging condition（150 ℃/24 h ＋ 180 ℃/12 h）, σ, θ＇（Al_2Cu） and T_1 phases are detected. Only the T_1 phases can be found in the T8 state alloy（6% pre-strain＋135 ℃/60 h）. The failure modes of alloy in T6 and duplex aging conditions are dimple-intergranular fracture, while typical quasi-cleavage fracture in T8 condition.
基金financially supported by the National Science Fund for Distinguished Young Scholars of China(51525204)the National Natural Science Foundation of China(51702229)。
文摘本文利用一种新的聚苯乙烯(PS)微乳液的凝胶化现象,制备了结构稳定的PS凝胶,并通过可控的毛细收缩过程获得了具有不同孔隙结构的PS块体.对PS微乳液的凝胶化机制的系统研究表明,在PS微乳液中加入适量特定的水溶性有机溶剂后,可实现PS微乳液的破乳,PS乳胶粒子周围的表面活性剂完全解吸附,并自发团聚成二次颗粒,在适当温度条件下可通过分子链缠结组装形成三维多孔凝胶.不同溶剂实现PS微乳液凝胶化的能力可以通过d2T/η参数的大小衡量和评估.通过进一步调整成胶时间与溶剂置换程度,PS凝胶可在后续的干燥过程中实现不同程度的收缩,从而得到密度范围在0.06–1.14 g cm^(-3)的多孔或致密PS块体.这种PS凝胶化策略是一种简单高效的PS成型方法,避免了成型设备、模板、成孔剂以及大量表面活性剂的应用,有望成为制备功能高分子聚合物块体材料的新方法.