Influence of three different rolling routes on mechanical anisotropy and formability of commercially pure titanium sheetwas investigated.Route A and Route B are unidirectional rolling(UR)where the rolling direction is...Influence of three different rolling routes on mechanical anisotropy and formability of commercially pure titanium sheetwas investigated.Route A and Route B are unidirectional rolling(UR)where the rolling direction is along initial rolling direction(RD)and transverse direction(TD),respectively.Route C is cross rolling(CR)where the rolling direction is changed by90°aftereach rolling pass.The microstructure and texture,tensile mechanical properties including strength and elongation,and also theanisotropy of the UR and CR sheets were investigated at room temperature.The XRD results indicate that the texture intensity ofrolled samples gradually weakens from Route A to Route C.Compared with Route A and Route B rolled samples,the Route C rolledsamples show a smaller planar anisotropy.The deep drawing tests reveal that cross rolling can avoid the occurrence of earing.Erichsen tests indicate that rolling routes have an effect on stretch formability of pure titanium sheet.展开更多
基金Project(CDJZR14130009) supported by the Fundamental Research Funds for the Central Universities,ChinaProject(CSTC2012GGB50003) supported by the Scientific and Technological Program of Chongqing Science and Technology Commission,ChinaProject(CSCT2014FAZKTJCSF50004) supported by the Demonstrative Project of Chongqing Science and Technology Commission,China
文摘Influence of three different rolling routes on mechanical anisotropy and formability of commercially pure titanium sheetwas investigated.Route A and Route B are unidirectional rolling(UR)where the rolling direction is along initial rolling direction(RD)and transverse direction(TD),respectively.Route C is cross rolling(CR)where the rolling direction is changed by90°aftereach rolling pass.The microstructure and texture,tensile mechanical properties including strength and elongation,and also theanisotropy of the UR and CR sheets were investigated at room temperature.The XRD results indicate that the texture intensity ofrolled samples gradually weakens from Route A to Route C.Compared with Route A and Route B rolled samples,the Route C rolledsamples show a smaller planar anisotropy.The deep drawing tests reveal that cross rolling can avoid the occurrence of earing.Erichsen tests indicate that rolling routes have an effect on stretch formability of pure titanium sheet.