Low temperature prepared(La_(0.8)Sr_(0.2))_(0.9)MnO_3-δ-Y_(0.15)Zr_(0.85)O_(1.93)(LSM-YSZ) nano-composite cathode has high three-phase boundary(TPB) density and shows higher oxygen reduction reaction(ORR) activity th...Low temperature prepared(La_(0.8)Sr_(0.2))_(0.9)MnO_3-δ-Y_(0.15)Zr_(0.85)O_(1.93)(LSM-YSZ) nano-composite cathode has high three-phase boundary(TPB) density and shows higher oxygen reduction reaction(ORR) activity than traditional LSM-YSZ cathode at reduced temperatures. But the weak connection between cathode and electrolyte due to low sintering temperature restrains the performance of LSM-YSZ nano-composite cathode. A YSZ interlayer, consisted of nanoparticles smaller than 10 nm, is introduced by spinning coating hydrolyzed YSZ sol solution on electrolyte and sintering at 800 °C. The thickness of the interlayer is about 150 nm. The YSZ interlayer intimately adheres to the electrolyte and shows obvious agglomeration with LSM-YSZ nano-composite cathode. The power densities of the cell with interlayer are 0.83, 0.46 and 0.21 W/cm^2 under 0.7 V at 800, 700 and 600 °C, respectively, which are 36%, 48% and 50% improved than that of original cell. The interlayer introduction slightly increases the ohmic resistance but significantly decreases the polarization resistance. The depressed high frequency arcs of impedance spectra suggest that the oxygen incorporation kinetics are enhanced at the boundary of YSZ interlayer and LSM-YSZ nanocomposite cathode, contributing to improved electrochemical performance of the cell with interlayer.展开更多
A composite interlayer comprised of gadolinia doped ceria(GDC) and Co/Fe oxide was prepared and investigated for solid oxide electrolysis cell with yttrium stabilized zirconia(YSZ) electrolyte and La_(0.6)Sr_(0.4)Co_(...A composite interlayer comprised of gadolinia doped ceria(GDC) and Co/Fe oxide was prepared and investigated for solid oxide electrolysis cell with yttrium stabilized zirconia(YSZ) electrolyte and La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_(3-δ)(LSCF) anode. The interlayer was constructed of a base layer of GDC and a top layer of discrete Co_3O_4/FeCo_2O_4 particles. The presence of the GDC layer drastically alleviated the undesired reactions between LSCF and YSZ, and the presence of Co/Fe oxide led to further performance improvement. At 800 °C and 45% humidity, the cell with 70% Co/Fe-GDC interlayer achieved 0.98 A/cm^2 at 1.18 V, 14% higher than the cell without Co/Fe oxide. Electrochemical impedance spectroscopy(EIS) revealed that with higher Co/Fe content, both the ohmic resistance and the polarization resistance of the cell were reduced. It is suggested that Co/Fe oxide can react with the Sr species segregated from LSCF and Sr_(1-x)(Co,Fe)O_(3-δ), a compound with high catalytic activity and electronic conductivity. The Sr-capturing ability of Co/Fe oxide in combination with the Sr-blocking ability of GDC layer can effectively suppress the undesired reaction between LSCF and YSZ, and consequently improve the cell performance.展开更多
基金financial supports from the National Natural Science Foundation of China (No.21506208,21376238,21476230,91534128)DICP DMTO201405
文摘Low temperature prepared(La_(0.8)Sr_(0.2))_(0.9)MnO_3-δ-Y_(0.15)Zr_(0.85)O_(1.93)(LSM-YSZ) nano-composite cathode has high three-phase boundary(TPB) density and shows higher oxygen reduction reaction(ORR) activity than traditional LSM-YSZ cathode at reduced temperatures. But the weak connection between cathode and electrolyte due to low sintering temperature restrains the performance of LSM-YSZ nano-composite cathode. A YSZ interlayer, consisted of nanoparticles smaller than 10 nm, is introduced by spinning coating hydrolyzed YSZ sol solution on electrolyte and sintering at 800 °C. The thickness of the interlayer is about 150 nm. The YSZ interlayer intimately adheres to the electrolyte and shows obvious agglomeration with LSM-YSZ nano-composite cathode. The power densities of the cell with interlayer are 0.83, 0.46 and 0.21 W/cm^2 under 0.7 V at 800, 700 and 600 °C, respectively, which are 36%, 48% and 50% improved than that of original cell. The interlayer introduction slightly increases the ohmic resistance but significantly decreases the polarization resistance. The depressed high frequency arcs of impedance spectra suggest that the oxygen incorporation kinetics are enhanced at the boundary of YSZ interlayer and LSM-YSZ nanocomposite cathode, contributing to improved electrochemical performance of the cell with interlayer.
基金supported by the National Natural Science Foundation of China (Nos. 21506208, 21476230 and 21376238)DICP DMTO201405
文摘A composite interlayer comprised of gadolinia doped ceria(GDC) and Co/Fe oxide was prepared and investigated for solid oxide electrolysis cell with yttrium stabilized zirconia(YSZ) electrolyte and La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_(3-δ)(LSCF) anode. The interlayer was constructed of a base layer of GDC and a top layer of discrete Co_3O_4/FeCo_2O_4 particles. The presence of the GDC layer drastically alleviated the undesired reactions between LSCF and YSZ, and the presence of Co/Fe oxide led to further performance improvement. At 800 °C and 45% humidity, the cell with 70% Co/Fe-GDC interlayer achieved 0.98 A/cm^2 at 1.18 V, 14% higher than the cell without Co/Fe oxide. Electrochemical impedance spectroscopy(EIS) revealed that with higher Co/Fe content, both the ohmic resistance and the polarization resistance of the cell were reduced. It is suggested that Co/Fe oxide can react with the Sr species segregated from LSCF and Sr_(1-x)(Co,Fe)O_(3-δ), a compound with high catalytic activity and electronic conductivity. The Sr-capturing ability of Co/Fe oxide in combination with the Sr-blocking ability of GDC layer can effectively suppress the undesired reaction between LSCF and YSZ, and consequently improve the cell performance.