REBa_(2)Cu_(3)O_(7−δ)(REBCO,RE=rare earth)tapes doped with 5%and 15%Zr have been scaled up to lengths more than 40 m in a pilot‐scale advanced metal organic chemical vapor deposition(A‐MOCVD)tool.The precursor comp...REBa_(2)Cu_(3)O_(7−δ)(REBCO,RE=rare earth)tapes doped with 5%and 15%Zr have been scaled up to lengths more than 40 m in a pilot‐scale advanced metal organic chemical vapor deposition(A‐MOCVD)tool.The precursor compositions used for the long tapes were guided by a study of the influence of(Ba+dopant)/Cu content on the critical current density(Jc)of 5 and 15 mol.%Hf‐and Zr‐added tapes at 4.2 K and 13 T.The 40‐mlong tapes exhibited a critical current(Ic)over 4,000 A/12 mm at 4.2 K and 13 T as well as over 1,400 A/12 mm at 20 K and 20 T.The critical current densities of a 40‐m‐long tape doped with 5%Zr at 4.2 K measured at the National High Magnetic Field Laboratory(NHMFL)were>10 MAcm^(−2)and>5 MAcm^(−2)at 14 T and 30 T,respectively,which are over three times those of commercial REBCO tapes.The infield Jc of 5%Zradded 40‐m‐long tapes was similar to those of previously‐reported high‐performance short samples made with 15%Zr or Hf.These results demonstrate the excellent potential of A‐MOCVD for manufacturing high Ic REBCO tapes for use in ultrahigh‐field magnet applications.展开更多
基金funded by awards DE‐EE0007869 from the Department of Energy Advanced Materials and Manufacturing Technology Office and DE‐SC0016220 from the Department of Energy Office of ScienceThe measurements at NHMFL,Tallahassee was supported by NSF award DMR‐1644779。
文摘REBa_(2)Cu_(3)O_(7−δ)(REBCO,RE=rare earth)tapes doped with 5%and 15%Zr have been scaled up to lengths more than 40 m in a pilot‐scale advanced metal organic chemical vapor deposition(A‐MOCVD)tool.The precursor compositions used for the long tapes were guided by a study of the influence of(Ba+dopant)/Cu content on the critical current density(Jc)of 5 and 15 mol.%Hf‐and Zr‐added tapes at 4.2 K and 13 T.The 40‐mlong tapes exhibited a critical current(Ic)over 4,000 A/12 mm at 4.2 K and 13 T as well as over 1,400 A/12 mm at 20 K and 20 T.The critical current densities of a 40‐m‐long tape doped with 5%Zr at 4.2 K measured at the National High Magnetic Field Laboratory(NHMFL)were>10 MAcm^(−2)and>5 MAcm^(−2)at 14 T and 30 T,respectively,which are over three times those of commercial REBCO tapes.The infield Jc of 5%Zradded 40‐m‐long tapes was similar to those of previously‐reported high‐performance short samples made with 15%Zr or Hf.These results demonstrate the excellent potential of A‐MOCVD for manufacturing high Ic REBCO tapes for use in ultrahigh‐field magnet applications.