The solubility of a direct arylation polycondensation(DArP)synthesized conjugated polymer,i.e.,poly(3,6-bis(furan-2-yl)-2,5-bis(4-tetradecyloctadecyl)-pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione-alt-1,2-bis(3,4-d ifl uorot...The solubility of a direct arylation polycondensation(DArP)synthesized conjugated polymer,i.e.,poly(3,6-bis(furan-2-yl)-2,5-bis(4-tetradecyloctadecyl)-pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione-alt-1,2-bis(3,4-d ifl uorothien-2-yl)ethene)(PFuD PP-4FTVT),in variou s organic solvents was studied.The polymer is soluble in 3-methylcyclohexanone(3-MC),a green solvent from peppermint oil,besides other solvents such as anisole,cyclopentyl methyl ether(CPME)and o-dichlorobenzene(o-DCB),etc.Based on the Hansen solu bility parameters(HSP)analysis,3-MC is identified as a"marginal solvent"of PFuDPP-4FTVT.The morphology of the spin-coated films with 3-MC as the solvent strongly correlated with the solution preparation conditions.With a 3-MC solution aged for 3 h at 70℃,n-channel organic thin-film transistors(OTFTs)with electron mobility(μe)above 1 cm^(2)·V^(-1)·s^(-1) and current on/off ratio(Ion/Ioff)higher than 105 were fabricated by spin-coating.This is the first report on high mobility conjugated polymers for OTFTs processible with natu rally occurred green solvent.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.51933008 and 52121002)the Fundamental Research Funds for the Central Universities。
文摘The solubility of a direct arylation polycondensation(DArP)synthesized conjugated polymer,i.e.,poly(3,6-bis(furan-2-yl)-2,5-bis(4-tetradecyloctadecyl)-pyrrolo[3,4-c]pyrrole-1,4(2H,5H)-dione-alt-1,2-bis(3,4-d ifl uorothien-2-yl)ethene)(PFuD PP-4FTVT),in variou s organic solvents was studied.The polymer is soluble in 3-methylcyclohexanone(3-MC),a green solvent from peppermint oil,besides other solvents such as anisole,cyclopentyl methyl ether(CPME)and o-dichlorobenzene(o-DCB),etc.Based on the Hansen solu bility parameters(HSP)analysis,3-MC is identified as a"marginal solvent"of PFuDPP-4FTVT.The morphology of the spin-coated films with 3-MC as the solvent strongly correlated with the solution preparation conditions.With a 3-MC solution aged for 3 h at 70℃,n-channel organic thin-film transistors(OTFTs)with electron mobility(μe)above 1 cm^(2)·V^(-1)·s^(-1) and current on/off ratio(Ion/Ioff)higher than 105 were fabricated by spin-coating.This is the first report on high mobility conjugated polymers for OTFTs processible with natu rally occurred green solvent.