In recent years,much research has been suggested and examined for the development of tissue engineering scaffolds to promote cellular behaviors.In our study,RGD peptide and graphene oxide(GO)co-functionalized poly(lac...In recent years,much research has been suggested and examined for the development of tissue engineering scaffolds to promote cellular behaviors.In our study,RGD peptide and graphene oxide(GO)co-functionalized poly(lactide-co-glycolide,PLGA)(RGD-GO-PLGA)nanofiber mats were fabricated via electrospinning,and their physicochemical and thermal properties were characterized to explore their potential as biofunctional scaffolds for vascular tissue engineering.Scanning electron microscopy images revealed that the RGD-GO-PLGA nanofiber mats were readily fabricated and composed of randomoriented electrospun nanofibers with average diameter of 558nm.The successful co-functionalization of RGD peptide and GO into the PLGA nanofibers was confirmed by Fourier-transform infrared spectroscopic analysis.Moreover,the surface hydrophilicity of the nanofiber mats was markedly increased by co-functionalizing with RGD peptide and GO.It was found that the mats were thermally stable under the cell culture condition.Furthermore,the initial attachment and proliferation of primarily cultured vascular smoothmuscle cells(VSMCs)on the RGD-GO-PLGA nanofibermats were evaluated.It was revealed that the RGD-GO-PLGA nanofibermats can effectively promote the growth of VSMCs.In conclusion,our findings suggest that the RGD-GO-PLGA nanofiber mats can be promising candidates for tissue engineering scaffolds effective for the regeneration of vascular smooth muscle.展开更多
In the present study,we report a fabrication of dual-mode carbon coated gadolinia C@Gd_(2)O_(3)particles by a facile hydrothermal synthesis method without using any organic solvents.The prepared C@Gd_(2)O_(3)particles...In the present study,we report a fabrication of dual-mode carbon coated gadolinia C@Gd_(2)O_(3)particles by a facile hydrothermal synthesis method without using any organic solvents.The prepared C@Gd_(2)O_(3)particles have a core-shell structure and a narrow size distribution in the range of 261±27 nm.The fluorescent properties of the prepared C@Gd_(2)O_(3)particles were accessed by a room-temperature photoluminescence study,while the longitudinal relaxivity(r1)was examined by using a clinical 1.5 T MRI scanner.A murine fibroblast L-929 cell line was used to examine the cytotoxicity and capability of the prepared C@Gd_(2)O_(3)particles for the fluorescent labeling.The obtained results show that the prepared C@Gd_(2)O_(3)particles could be used as a dual-mode contrast agent for magnetic resonance and fluorescence imaging.展开更多
基金This study was supported by the Bio&Medical Technology Development Program of the National Research Foundation(NRF)funded by the Korean government(MEST)(No.2015M3A9E2028643)Basic Science Research Program through the NRF of Korea funded by the Ministry of Education(No.2016R1D1A1B03931076).
文摘In recent years,much research has been suggested and examined for the development of tissue engineering scaffolds to promote cellular behaviors.In our study,RGD peptide and graphene oxide(GO)co-functionalized poly(lactide-co-glycolide,PLGA)(RGD-GO-PLGA)nanofiber mats were fabricated via electrospinning,and their physicochemical and thermal properties were characterized to explore their potential as biofunctional scaffolds for vascular tissue engineering.Scanning electron microscopy images revealed that the RGD-GO-PLGA nanofiber mats were readily fabricated and composed of randomoriented electrospun nanofibers with average diameter of 558nm.The successful co-functionalization of RGD peptide and GO into the PLGA nanofibers was confirmed by Fourier-transform infrared spectroscopic analysis.Moreover,the surface hydrophilicity of the nanofiber mats was markedly increased by co-functionalizing with RGD peptide and GO.It was found that the mats were thermally stable under the cell culture condition.Furthermore,the initial attachment and proliferation of primarily cultured vascular smoothmuscle cells(VSMCs)on the RGD-GO-PLGA nanofibermats were evaluated.It was revealed that the RGD-GO-PLGA nanofibermats can effectively promote the growth of VSMCs.In conclusion,our findings suggest that the RGD-GO-PLGA nanofiber mats can be promising candidates for tissue engineering scaffolds effective for the regeneration of vascular smooth muscle.
基金supported by the 2014 Post-Doc,Development Program of Pusan National Universitysupported by the National Research Foundation of Korea(NRF)grant funded by the Korea government(MSIP)(No.2014R1A2A1A11051146).
文摘In the present study,we report a fabrication of dual-mode carbon coated gadolinia C@Gd_(2)O_(3)particles by a facile hydrothermal synthesis method without using any organic solvents.The prepared C@Gd_(2)O_(3)particles have a core-shell structure and a narrow size distribution in the range of 261±27 nm.The fluorescent properties of the prepared C@Gd_(2)O_(3)particles were accessed by a room-temperature photoluminescence study,while the longitudinal relaxivity(r1)was examined by using a clinical 1.5 T MRI scanner.A murine fibroblast L-929 cell line was used to examine the cytotoxicity and capability of the prepared C@Gd_(2)O_(3)particles for the fluorescent labeling.The obtained results show that the prepared C@Gd_(2)O_(3)particles could be used as a dual-mode contrast agent for magnetic resonance and fluorescence imaging.