Duplexα/β-SiAlON ceramic cutting inserts(30α:70β)were synthesized by microwave sintering.The effects of solid solution parameters(m,n,z),synthesis temperature,and amount of excess Y_(2)O_(3) synthesis additive on ...Duplexα/β-SiAlON ceramic cutting inserts(30α:70β)were synthesized by microwave sintering.The effects of solid solution parameters(m,n,z),synthesis temperature,and amount of excess Y_(2)O_(3) synthesis additive on phase assemblage,microstructure,mechanical properties,and cutting performance were systematically investigated.It was found that increasing m value could improve the formation ofαphase while high z value over 1.0 resulted in the dissolution ofαphase intoβphase and intergranular phase.Increasing the amount of excess Y_(2)O_(3) could promote densification and elongatedβgrain growth;however,the excess Y_(2)O_(3) amount above 4 wt%resulted in substantial crystallization of M'SS phase,thus declining the mechanical properties and wear resistance.The microwave-synthesizedα/β-SiAlON cutting insert with modified parameters(m=1.7,n=1.0,z=0.7,and 3 wt%excess Y_(2)O_(3))was obtained with optimal comprehensive properties,whose tool life was found to increase by approximately 75%in high-speed milling of Inconel 718 superalloy compared to the commercialα/β-SiAlON cutting insert.展开更多
基金The work is supported by the National Natural Science Foundation of China(Nos.51875291 and 52075266)the Excellent Youth Fund of Jiangsu Province(No.BK20190070)the Fundamental Research Funds for the Central Universities(No.30920032206).
文摘Duplexα/β-SiAlON ceramic cutting inserts(30α:70β)were synthesized by microwave sintering.The effects of solid solution parameters(m,n,z),synthesis temperature,and amount of excess Y_(2)O_(3) synthesis additive on phase assemblage,microstructure,mechanical properties,and cutting performance were systematically investigated.It was found that increasing m value could improve the formation ofαphase while high z value over 1.0 resulted in the dissolution ofαphase intoβphase and intergranular phase.Increasing the amount of excess Y_(2)O_(3) could promote densification and elongatedβgrain growth;however,the excess Y_(2)O_(3) amount above 4 wt%resulted in substantial crystallization of M'SS phase,thus declining the mechanical properties and wear resistance.The microwave-synthesizedα/β-SiAlON cutting insert with modified parameters(m=1.7,n=1.0,z=0.7,and 3 wt%excess Y_(2)O_(3))was obtained with optimal comprehensive properties,whose tool life was found to increase by approximately 75%in high-speed milling of Inconel 718 superalloy compared to the commercialα/β-SiAlON cutting insert.