A novel V-doped CeO_(2)-supported alkali-activated-steel-slag-based catalyst(V-CeO_(2)/AC)for photocatalytic decomposition of water to hydrogen was prepared via co-impregnation method.The chemical composition,mineral ...A novel V-doped CeO_(2)-supported alkali-activated-steel-slag-based catalyst(V-CeO_(2)/AC)for photocatalytic decomposition of water to hydrogen was prepared via co-impregnation method.The chemical composition,mineral phase,morphology,and optical performances of the synthesized catalyst samples were characterized by XRF,XRD,SEM,UV-Vis DRS,and so on.XRD and SEM results show that calcium silicate hydrate(Ca1.5SiO3.5·xH2O)mineral phase is formed in the carrier sample,and the prepared catalyst specimens are made up of approximately 50 nm particles.After 6 hours of xenon lamp irradiation,the catalyst supported on V-doped 8wt%CeO_(2) exhibits the highest photocatalytic hydrogen production activity(8292μmol/g),which is attributed to the interaction between the V-doped CeO_(2) active components and FeO existed in catalyst carrier.A possible photocatalytic decomposition of water for hydrogen production mechanism over the V-8CeO_(2)/AC catalyst was proposed.展开更多
基金Funded by the National Natural Science Foundation of China(No.51372197)the Basic Research Plan of Natural Science of Shaanxi Province(No.2020JQ-754)+4 种基金the Key Innovation Team of Shaanxi Province(No.2014KCT-04)the Special Project of Shaanxi Province(No.19JK0490)the Construction and Promotion of Highlevel Achievements in Material Science and Engineering Discipline of Xi’an University of Science and Technology(No.2040519061)the Study on Preparation and Properties of New Solid-wastebased Cementitious Materials(No.6000190120)the Xi’an University of Science and Technology Doctoral Start-up Project(No.2018QDJ011)。
文摘A novel V-doped CeO_(2)-supported alkali-activated-steel-slag-based catalyst(V-CeO_(2)/AC)for photocatalytic decomposition of water to hydrogen was prepared via co-impregnation method.The chemical composition,mineral phase,morphology,and optical performances of the synthesized catalyst samples were characterized by XRF,XRD,SEM,UV-Vis DRS,and so on.XRD and SEM results show that calcium silicate hydrate(Ca1.5SiO3.5·xH2O)mineral phase is formed in the carrier sample,and the prepared catalyst specimens are made up of approximately 50 nm particles.After 6 hours of xenon lamp irradiation,the catalyst supported on V-doped 8wt%CeO_(2) exhibits the highest photocatalytic hydrogen production activity(8292μmol/g),which is attributed to the interaction between the V-doped CeO_(2) active components and FeO existed in catalyst carrier.A possible photocatalytic decomposition of water for hydrogen production mechanism over the V-8CeO_(2)/AC catalyst was proposed.