In the paper, the results of investigations of temperature and frequency dependences of dielectric permeability and dielectric loss of compositions LDPE + xvol%Bi<sub>2</sub>Te<sub>3</sub> are ...In the paper, the results of investigations of temperature and frequency dependences of dielectric permeability and dielectric loss of compositions LDPE + xvol%Bi<sub>2</sub>Te<sub>3</sub> are stated. The investigations were carried out at frequency 10 – 10<sup>5</sup> Hz and temperature 20°C - 150°C intervals, respectively. It was revealed that increase of percentage of the filler Bi<sub>2</sub>Te<sub>3</sub> in the matrix, reduces to increase of dielectric permeability and dielectric loss of composites LDPE + xvol%Bi<sub>2</sub>Te<sub>3</sub> in connection with the change reducing to Maxwell-Wagner’s volume polarization and emergence of comparative strong inner field in semiconductor clusters.展开更多
The paper presents the results of studies surface microrelief, frequency-temperature characteristics of the imaginary part of the dielectric permittivity and dielectric loss of PE+TlInSe2 composite materials in 25。C ...The paper presents the results of studies surface microrelief, frequency-temperature characteristics of the imaginary part of the dielectric permittivity and dielectric loss of PE+TlInSe2 composite materials in 25。C - 150。C temperature and 25 Hz - 1 MHz frequency range before and after application of the aluminum nano-particles with a size of 50 nm. The change in the amount of semicon-ductor filler TlInSe2 and aluminum nano-particles changes the state of the surface and the frequency-temperature characteristics of composite materials PE+xvol.%TlInSe2, which allows to obtain composites with the desired dielectric permittivity and dielectric loss.展开更多
The purpose of the paper is to study the effect of gamma irradiation on the temperature dependence of the dielectric constant and dielectric loss (tanδ) of composite materials PE + x vol% (0≤ x ≤ 10). Measurements ...The purpose of the paper is to study the effect of gamma irradiation on the temperature dependence of the dielectric constant and dielectric loss (tanδ) of composite materials PE + x vol% (0≤ x ≤ 10). Measurements are carried out with an alternating current at a frequency of 1 kHz using the measuring bridge E-20. Measurements are carried out at temperature range 300 - 450 K, irradiated at doses of 50, 100 and 150 kGy. It is revealed that in all irradiated samples with increasing volumetric filler content increase the dielectric characteristics of composites PE + x vol%. TlGaSe2. Temperature variation of the dielectric parameters, after gamma irradiation are the result of occurring in the electron-ion and polarization at the interface of the matrix polymer with filler of TlGaSe2.展开更多
文摘In the paper, the results of investigations of temperature and frequency dependences of dielectric permeability and dielectric loss of compositions LDPE + xvol%Bi<sub>2</sub>Te<sub>3</sub> are stated. The investigations were carried out at frequency 10 – 10<sup>5</sup> Hz and temperature 20°C - 150°C intervals, respectively. It was revealed that increase of percentage of the filler Bi<sub>2</sub>Te<sub>3</sub> in the matrix, reduces to increase of dielectric permeability and dielectric loss of composites LDPE + xvol%Bi<sub>2</sub>Te<sub>3</sub> in connection with the change reducing to Maxwell-Wagner’s volume polarization and emergence of comparative strong inner field in semiconductor clusters.
文摘The paper presents the results of studies surface microrelief, frequency-temperature characteristics of the imaginary part of the dielectric permittivity and dielectric loss of PE+TlInSe2 composite materials in 25。C - 150。C temperature and 25 Hz - 1 MHz frequency range before and after application of the aluminum nano-particles with a size of 50 nm. The change in the amount of semicon-ductor filler TlInSe2 and aluminum nano-particles changes the state of the surface and the frequency-temperature characteristics of composite materials PE+xvol.%TlInSe2, which allows to obtain composites with the desired dielectric permittivity and dielectric loss.
文摘The purpose of the paper is to study the effect of gamma irradiation on the temperature dependence of the dielectric constant and dielectric loss (tanδ) of composite materials PE + x vol% (0≤ x ≤ 10). Measurements are carried out with an alternating current at a frequency of 1 kHz using the measuring bridge E-20. Measurements are carried out at temperature range 300 - 450 K, irradiated at doses of 50, 100 and 150 kGy. It is revealed that in all irradiated samples with increasing volumetric filler content increase the dielectric characteristics of composites PE + x vol%. TlGaSe2. Temperature variation of the dielectric parameters, after gamma irradiation are the result of occurring in the electron-ion and polarization at the interface of the matrix polymer with filler of TlGaSe2.