The oxidation behavior of Ni-based superalloy GH4742 exposed to water vapor was investigated at 900-1100℃for 50 h in Ar+20%H_(2)O,with Ar+20%O_(2)included for comparison.The presence of H_(2)O is adverse to formation...The oxidation behavior of Ni-based superalloy GH4742 exposed to water vapor was investigated at 900-1100℃for 50 h in Ar+20%H_(2)O,with Ar+20%O_(2)included for comparison.The presence of H_(2)O is adverse to formation of continuous Cr_(2)O_(3)oxide layer but contributes to generation of big voids.Based on this,Ni^(2+)and Co^(2+)are more easily to diffuse towards the outermost oxide layer(OOL),forming non-protective Ni-and Co-rich oxides with high proportion.This leads to a higher weight gain in Ar+20%H_(2)O than that in Ar+20%O_(2).At elevated temperatures,the spallation of oxide scale occurs while the consumption of Cr is reduced in Ar+20%H_(2)O,and the contents of Ni-and Co-rich oxides at this moment are reduced in the OOL.The oxidation mechanism was also discussed.展开更多
基金supported by the National Key R&D Program of China(No.2021YFB3700400)National Natural Science Foundation of China(Nos.52074030,51904021,52174294).
文摘The oxidation behavior of Ni-based superalloy GH4742 exposed to water vapor was investigated at 900-1100℃for 50 h in Ar+20%H_(2)O,with Ar+20%O_(2)included for comparison.The presence of H_(2)O is adverse to formation of continuous Cr_(2)O_(3)oxide layer but contributes to generation of big voids.Based on this,Ni^(2+)and Co^(2+)are more easily to diffuse towards the outermost oxide layer(OOL),forming non-protective Ni-and Co-rich oxides with high proportion.This leads to a higher weight gain in Ar+20%H_(2)O than that in Ar+20%O_(2).At elevated temperatures,the spallation of oxide scale occurs while the consumption of Cr is reduced in Ar+20%H_(2)O,and the contents of Ni-and Co-rich oxides at this moment are reduced in the OOL.The oxidation mechanism was also discussed.