The isothermal tetragonal-to-monoclinic phase transformation of 3 mol fraction Y2O3-ZrO2 ceramics contain- ing different amounts of Al2O3 during ageing in water at 130℃ for periods of time up to 40 h was investigated...The isothermal tetragonal-to-monoclinic phase transformation of 3 mol fraction Y2O3-ZrO2 ceramics contain- ing different amounts of Al2O3 during ageing in water at 130℃ for periods of time up to 40 h was investigated to explore the effect of Al2O3 addition on this transformation. The propagation of the transformation into the specimen interiors was suppressed by the addition of Al2O3. The transformation kinetics showed a nucleation and growth mechanism on the specimen surface to be dominant in the low temperature ageing in water environment.展开更多
The low temperature aging behavior of polycrystalline tetragonal zirconia was investigated to explore the effects on phase transformation occurring during the process. XRD analysis was conducted for the phase identifi...The low temperature aging behavior of polycrystalline tetragonal zirconia was investigated to explore the effects on phase transformation occurring during the process. XRD analysis was conducted for the phase identification and the tetragonal to monoclinic phase transformation was determined. The aging of tetragonal zirconia polycrystals doped with 3 mol% Y203 triggers tetragonal to monoclinic phase transformation on the surface of the specimen only, while the penetration inside the bulk of the specimen is very limited. A slight decrease in the mechanical properties was also observed after aging for 40 h. The transformation kinetics show a nucleation and growth mechanism on the specimen surface to be dominant in the low temperature aging in water environment.展开更多
文摘The isothermal tetragonal-to-monoclinic phase transformation of 3 mol fraction Y2O3-ZrO2 ceramics contain- ing different amounts of Al2O3 during ageing in water at 130℃ for periods of time up to 40 h was investigated to explore the effect of Al2O3 addition on this transformation. The propagation of the transformation into the specimen interiors was suppressed by the addition of Al2O3. The transformation kinetics showed a nucleation and growth mechanism on the specimen surface to be dominant in the low temperature ageing in water environment.
文摘The low temperature aging behavior of polycrystalline tetragonal zirconia was investigated to explore the effects on phase transformation occurring during the process. XRD analysis was conducted for the phase identification and the tetragonal to monoclinic phase transformation was determined. The aging of tetragonal zirconia polycrystals doped with 3 mol% Y203 triggers tetragonal to monoclinic phase transformation on the surface of the specimen only, while the penetration inside the bulk of the specimen is very limited. A slight decrease in the mechanical properties was also observed after aging for 40 h. The transformation kinetics show a nucleation and growth mechanism on the specimen surface to be dominant in the low temperature aging in water environment.