SmCo5/Fe65Co35 and SmCo5/Fe spring exchange magnets are fabricated by dc magnetron sputtering on MgO substrates and 100-nm-thick Si3N4 membranes, respectively. The base pressure of sputtering chamber is kept below 10^...SmCo5/Fe65Co35 and SmCo5/Fe spring exchange magnets are fabricated by dc magnetron sputtering on MgO substrates and 100-nm-thick Si3N4 membranes, respectively. The base pressure of sputtering chamber is kept below 10^-7 Tort, and Ar pressure is 3 to 8mTorr. The samples are characterized by an x-ray diffractometer, a superconducting quantum interference magnetometer, and high resolution magnetic soft x-ray microscopy. We obtain the complete exchange coupling and single phase behaviour of composite magnets. The （BH）max value achieved is 28.8 MGOe.展开更多
Trilayered Sm2Co7/Fe/Sm2Co7 spring exchange magnets are fabricated by dc magnetron sputtering on MgO substrates. Very thin layers （0.3-0.7 nm） of Cr and Ti are added at the interfaces of the two magnetic phases. The...Trilayered Sm2Co7/Fe/Sm2Co7 spring exchange magnets are fabricated by dc magnetron sputtering on MgO substrates. Very thin layers （0.3-0.7 nm） of Cr and Ti are added at the interfaces of the two magnetic phases. The thickness of StucCo7 is kept at 20nm and Fe at 6nm while the thickness of Cr and Ti are varied as 0.3, 0.5, and 0.7nm. The base pressure of sputtering chamber is kept below 10^-7 Torr and Ar pressure at 3-8m Torr. The samples are characterized by x-ray diffraction （XRD） and SQUID magnetometer. We report improvement in exchange coupling of nonacomposite magnets by addition of thin layers of Cr at interfaces.展开更多
文摘SmCo5/Fe65Co35 and SmCo5/Fe spring exchange magnets are fabricated by dc magnetron sputtering on MgO substrates and 100-nm-thick Si3N4 membranes, respectively. The base pressure of sputtering chamber is kept below 10^-7 Tort, and Ar pressure is 3 to 8mTorr. The samples are characterized by an x-ray diffractometer, a superconducting quantum interference magnetometer, and high resolution magnetic soft x-ray microscopy. We obtain the complete exchange coupling and single phase behaviour of composite magnets. The （BH）max value achieved is 28.8 MGOe.
文摘Trilayered Sm2Co7/Fe/Sm2Co7 spring exchange magnets are fabricated by dc magnetron sputtering on MgO substrates. Very thin layers （0.3-0.7 nm） of Cr and Ti are added at the interfaces of the two magnetic phases. The thickness of StucCo7 is kept at 20nm and Fe at 6nm while the thickness of Cr and Ti are varied as 0.3, 0.5, and 0.7nm. The base pressure of sputtering chamber is kept below 10^-7 Torr and Ar pressure at 3-8m Torr. The samples are characterized by x-ray diffraction （XRD） and SQUID magnetometer. We report improvement in exchange coupling of nonacomposite magnets by addition of thin layers of Cr at interfaces.