The ceramifiable polymer composite of MgO-Al_(2)O_(3)-SiO_(2)/boron phenolic resin(MAS/BPF)with 40wt%of inorganic fillers was calcined at 1200℃for different time to promote ceramification of ceramifiable composite an...The ceramifiable polymer composite of MgO-Al_(2)O_(3)-SiO_(2)/boron phenolic resin(MAS/BPF)with 40wt%of inorganic fillers was calcined at 1200℃for different time to promote ceramification of ceramifiable composite and improve heat resistance.The effects of different calcine time on the macroscopical morphology,mass loss,phase evolution,microstructure and chemical bond evolution of MAS/BPF composites were characterized by XRD,XPS,and SEM analyses.The experimental results reveal that the increase of calcine time result in the fewer holes,relatively denser and smoother top layer of MAS/BPF composites and protect the interior from deeper decomposition.The final residues of composites are amorphous carbon and C-O-Si-Al-Mg ceramic.And MAS/BPF composites show excellent mass stability,low shrinkage and self-supporting features after 2 h holding compared with BPF composites without 40wt%of inorganic fillers.展开更多
基金Funded by the Joint Fund of Ministry of Education for Equipment Pre-research(Nos.6141A02022250 and SAST2018-067)。
文摘The ceramifiable polymer composite of MgO-Al_(2)O_(3)-SiO_(2)/boron phenolic resin(MAS/BPF)with 40wt%of inorganic fillers was calcined at 1200℃for different time to promote ceramification of ceramifiable composite and improve heat resistance.The effects of different calcine time on the macroscopical morphology,mass loss,phase evolution,microstructure and chemical bond evolution of MAS/BPF composites were characterized by XRD,XPS,and SEM analyses.The experimental results reveal that the increase of calcine time result in the fewer holes,relatively denser and smoother top layer of MAS/BPF composites and protect the interior from deeper decomposition.The final residues of composites are amorphous carbon and C-O-Si-Al-Mg ceramic.And MAS/BPF composites show excellent mass stability,low shrinkage and self-supporting features after 2 h holding compared with BPF composites without 40wt%of inorganic fillers.